Three-dimensional N-doped super-hydrophilic carbon electrodes with porosity tailored by Cu<sub>2</sub>O template-assisted electrochemical oxidation to improve the performance of electrical double-layer capacitors
نویسندگان
چکیده
Cu2O was used as a porosity adjustment template and assisted electrochemical oxidation to prepare three-dimensional N-doped superhydrophilic carbon electrodes, showing excellent performance in electric double layer capacitors.
منابع مشابه
Macroporous MnO2 Electrodes Obtained by Template Assisted Electrodeposition for Electrochemical Capacitors
Eletrodos macroporosos de MnO 2 foram preparados por eletrodeposição assistida por molde de partículas esféricas coloidais de poliestireno. A molhabilidade desses filmes foi estudada por medidas de ângulo de contato. Medidas de voltametria cíclica foram realizadas com o objetivo de estudar o seu comportamento como eletrodo para supercapacitores. A capacitância específica obtida foi cerca de 60%...
متن کاملNitrogen-enriched carbon electrodes in electrochemical capacitors: investigating accessible porosity using CM-SANS.
Carbon electrochemical capacitor electrodes containing nitrogen groups were studied with respect to their electrochemical behaviour, chemical composition and physical characteristics. Thermal treatment of nitrogen-enriched carbon materials in different atmospheres was used to control the specific type and concentration of nitrogen groups present, while importantly retaining similar pore size di...
متن کاملPreparation and Characterization of Reduced Graphene Oxide Doped in Sol-Gel Derived Silica for Application in Electrochemical Double-Layer Capacitors
In this study, a new graphene ceramic composite (GCC) was prepared based on the reduced grapheneoxide (rGO) doped in sol-gel derived silica. The GCC was prepared by dispersing rGO nanosheets intothe sol-gel precursors containing methyl triethoxysilane, methanol and hydrochloric acid solution.During an acid catalyzed hydrolyze reaction and gelation proc...
متن کاملSuperionic state in double-layer capacitors with nanoporous electrodes.
In recent experiments (Chmiola et al 2006 Science 313 1760; Largeot et al 2008 J. Am. Chem. Soc. 130 2730) an anomalous increase of the capacitance with a decrease of the pore size of a carbon-based porous electric double-layer capacitor has been observed. We explain this effect by image forces which exponentially screen out the electrostatic interactions of ions in the interior of a pore. Pack...
متن کاملElectrochemical characterization of carbon nanotubes as electrode in electrochemical double-layer capacitors
Carbon nanotubes uniformly 50 nm in diameter were directly grown on graphite foil. Cyclic voltammetry (CV) shows that the carbon nanotube /graphite foil electrode has a high specific capacitance (115.7 F/g at a scan rate of 100 mV/s) and exhibits typical double-layer behavior. A rectangular-shaped CV curve persists even at a scan rate of 100 mV/s in 1.0 M H SO aqueous solution, which suggests t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of materials chemistry. A, Materials for energy and sustainability
سال: 2021
ISSN: ['2050-7488', '2050-7496']
DOI: https://doi.org/10.1039/d0ta10294f