Transformation of Electrodeposited Cr Films Cased by Hydrogen Dissolution
نویسندگان
چکیده
منابع مشابه
Hydrogen Dissolution and Structural Changes in Electrodeposited Cr Films*
Effects of hydrogen on the structure of electrodeposited Cr films have been investigated by combining X-ray diffraction and thermal desorption spectroscopy, systematically varying the plating conditions. A large amount of hydrogen was dissolved at high current densities in a Cr-rich bath at low temperatures, and caused structural changes from bcc to hcp and fcc hydrides with increasing hydrogen...
متن کاملInvestigation of Tribological Behavior of Electrodeposited Cr, Co-Cr and Co-Cr/TiO2 Nano-Composite Coatings
Electrodeposition is a simple and economic technique for precision coating of different shaped substrates with pure metal, alloy or composite films. Dc electrodeposition was used to produce Cr, Co-Cr and Co-Cr/TiO2 nano-composite coatings from Cr(III) based electrolytes onto 316L SS substrates. The effects of TiO2 nanoparticles concentration on co-deposition of these particles along with Cr con...
متن کاملProperties of Electrodeposited WO3 Thin Films
Galvanostatic electrodeposition was used to produce transparent and amorphous WO3 films that showed color changes from clear to blue in response to the applied potential of ±1.0 V. The 61% in transmittance variation was measured at wavelength of 633 nm. The roughness of 16.7 nm was obtained by atomic force microscopy (AFM). The scanning electron microscopy (SEM) evidenced homogeneous morphology...
متن کاملAqueous Cr(VI) reduction by electrodeposited zero-valent iron at neutral pH: acceleration by organic matters.
This work investigated the effect of co-existing organic matters on aqueous Cr(VI) reduction by electrodeposited zero-valent iron (ED Fe(0)) at neutral pH. The ED Fe(0) prepared in a solution containing mixture of saccharin, L-ascorbic acid and sodium dodecyl sulfate showed higher activity in reducing the aqueous Cr(VI) at neutral pH than that prepared without any organic presence. XRD and SEM ...
متن کاملHydrogen Diffusion and Trapping in Electrodeposited Nickel
In an attempt to quantify grain boundary diffusion of hydrogen in nickel, permeation in electrodeposited foil has been investigated. Pinhole-free specimens were plated from a nickel sulfamate bath onto a reusable anodized titanium cathode. The microstructure was a mixture of regions of fine grains (diameters <0.1 tm) and individual grains up to 2 tm in diameter. The specimens were subjected to ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals
سال: 2004
ISSN: 0021-4876
DOI: 10.2320/jinstmet.68.552