Trend of Tape Casting Technology for Electronics.
نویسندگان
چکیده
منابع مشابه
TAPE CASTING OF NON-AQUEOUS HYDROXYAPATITE SLIPS
Thin sheets of hydroxyapatite were fabricated by tape casting process. The non-aqueoustape casting formulation was optimized by adjusting the concentration of organic additivesspecially those of binder and plasticizer in the slurry. The optimized slurry was cast on a glasscarrier using a designed laboratory scale doctor blade. Following a binder removal stage, thetapes were sintered at differen...
متن کاملPreparation of hexaferrite multilayers by tape casting
Tape casting technics were used to realize a screen with continuous change in characteristics. Different hexaferrite compositions owned by the Ba3C02-~Zn~Fe24041 (Z) family were synthetized by coprecipitation method and calcined at 1200 "C in air. Then a slurry containing this powder is slip casted using tape casting. The tapes are dried under magnetic fied in order to orient the magnetic plate...
متن کاملUltrasonic deagglomeration of AI2O3 and BaTiO3 for tape casting
Ultrasonic agitation is a very efficient method for deagglomeration and dispersion of ceramic slurries (alumina and barium titanate). The influence of parameters such as acoustic power, temperature, and treatment duration on the dispersion efficiency has been studied. For
متن کاملTechnology for the Production of Clean Electronics
This paper describes the experience gained in Sweden in connection with early phase-out of CFC-113 in the production engineering industry. It concentrates particularly on the phase-out of CFC-113 in the production of PCB assemblies, although parallel applications for cleaning of precision components, metal cleaning and : to some extent the phase-out of l,l,l-trichloroethane are also considered....
متن کاملEthanol-based Tape Casting Process of the Textured Bi0.5(Na0.80K0.20)0.5TiO3-BiFeO3 Ceramics
The rheological and tape casting behavior of ethanol-based Bi0.5(Na0.80K0.20)0.5TiO3-7 mol% BiFeO3 (BNKT-BF) slurries was investigated. The effect of sintering temperature profile on texture development with a preferred orientation was also studied. A 50 MPa pressure assisted three step sintering profile promoted extensive texture development together with densification. The role of BF as a sin...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Powder Technology, Japan
سال: 1991
ISSN: 0386-6157,1883-7239
DOI: 10.4164/sptj.28.759