Tribocorrosion behavior of Ti–C–O–N nanostructured thin films (black) for decorative applications
نویسندگان
چکیده
منابع مشابه
Magnetic Behavior of Surface Nanostructured 50-nm Nickel Thin Films
Thermally evaporated 50-nm nickel thin films coated on borosilicate glass substrates were nanostructured by excimer laser (0.5 J/cm(2), single shot), DC electric field (up to 2 kV/cm) and trench-template assisted technique. Nanoparticle arrays (anisotropic growth features) have been observed to form in the direction of electric field for DC electric field treatment case and ruptured thin film (...
متن کاملStudies on sol-gel dip-coated nanostructured ZnO thin films
Nanostructured ZnO thin films were prepared by sol-gel dip coating technique. Zinc acetate and ammonium hydroxide were used as precursors and ethanol was as solvent. Ammonium hydroxide (NH4OH) solution was added drop-wise under vigorous stirring to obtain the sol-gel of different pH (varying from 6.9 to 7.2). ZnO thin films were obtained by dipping the glass substrates for few seconds and then ...
متن کاملEffect of Annealing on Physical Properties of Cu2ZnSnS4 (CZTS) Thin Films for Solar Cell Applications
Cu2ZnSnS4 (CZTS) thin films were prepared by directly sputteringCu (In,Ga)Se2 quaternary target consisting of (Cu: 25%, Zn: 12.5%, Sn; 12.5%and S: 50%). The composition and structure of CZTS layers have beeninvestigated after annealing at 200 0C, 350 0C and 500 0C under vacuum. Theresults show that recrystallization of the CZTS thin film occurs and increasingthe grain size with a preferred orie...
متن کاملMultifunctional nanostructured Ti-Si-C thin films
In this Thesis, I have investigated multifunctional nanostructured Ti-Si-C thin films synthesized by magnetron sputtering in the substrate-temperature range from room temperature to 900 °C. The studies cover high-temperature growth of Ti3SiC2 and Ti4SiC3, low-temperature growth of Ti-Si-C nanocomposites, and Ti-Si-C-based multilayers, as well as their electrical, mechanical, and thermal-stabili...
متن کاملNanostructured FePt films for magnetic media applications
Smaller, faster, denser and cheaper magnetic disk drives are demanded for information storage using magnetic media. Increase in high areal density in magnetic recording requires small bit cells with very small grain size. The reduction of bit cell volume and grain size will eventually be constrained by the undesirable thermal instability of magnetization due to the superparamagnetic effect, thu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tribology International
سال: 2013
ISSN: 0301-679X
DOI: 10.1016/j.triboint.2013.06.003