Ultrasonic excitation induced nanocrystallization and toughening of Zr46.75Cu46.75Al6.5 bulk metallic glass
نویسندگان
چکیده
منابع مشابه
Ductile bulk metallic glass.
We report on experimental evidence of pronounced global plasticity measured in monolithic Pt57.5Cu14.7Ni5.3P22.5 bulk metallic glass under both bending and unconfined compression loading conditions. A plastic strain of 20% is measured, never before seen in metallic glasses. Also, permanent deformation and a strain exceeding 3% before failure is observed during bending of 4 mm thick samples. To ...
متن کاملBulk metallic glass matrix composites
Composites with a bulk metallic glass matrix were synthesized and characterized. This was made possible by the recent development of bulk metallic glasses that exhibit high resistance to crystallization in the undercooled liquid state. In this letter, experimental methods for processing metallic glass composites are introduced. Three different bulk metallic glass forming alloys were used as the...
متن کاملOut-of-plane magnetic patterning based on indentation-induced nanocrystallization of a metallic glass.
Periodic arrays of micrometer-sized ferromagnetic structures with perpendicular magnetic anisotropy are prepared by nanoindentation at the surface of a Fe(67.7)B(20)Cr(12)Nb(0.3) glassy ribbon initially showing in-plane magnetic anisotropy. The indented regions exhibit enhanced coercivity and saturation magnetization with respect to the surrounding nondeformed matrix. These effects are due to a...
متن کاملStrain rate induced crystallization in bulk metallic glass-forming liquid.
We report on the solidification of Au49, Ag5.5, Pd2.3, Cu26.9, Si16.3 bulk metallic glass under various strain rates. Using a copper mold casting technique with a low strain rate during solidification, this alloy is capable of forming glassy rods of at least 5 mm in diameter. Surprisingly, when the liquid alloy is splat cooled at much higher cooling rates and large strain rates, the solidified ...
متن کاملNew class of plastic bulk metallic glass.
An intrinsic plastic Cu(45)Zr(46)Al(7)Ti(2) bulk metallic glass (BMG) with high strength and superior compressive plastic strain of up to 32.5% was successfully fabricated by copper mold casting. The superior compressive plastic strain was attributed to a large amount of randomly distributed free volume induced by Ti minor alloying, which results in extensive shear band formation, branching, in...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Science & Technology
سال: 2020
ISSN: 1005-0302
DOI: 10.1016/j.jmst.2019.10.035