Wear Behaviour of A356/TiAl3 in Situ Composites Produced by Mechanical Alloying
نویسندگان
چکیده
منابع مشابه
Mechanical and Wear Properties of Al-Nip Composites Produced by ARB Process
In this research, Al-Ni particle composite strips are formed by accumulative roll bonding (ARB) process using Al strips and Ni powder. The rule of ARB cycles and volume percentage (Vol%) of Ni powder on the microstructure, wear resistance and mechanical properties of the formed composites are investigated. According to the tensile test results, the yield stress and tensile strengths of the Al -...
متن کاملinvestigation on heat treatment and mechanical behaviour of al2024/gr composites produced by in-situ powder metallurgy
in this study, al/gr composites with 5,10,15,20 weight percent of graphite were produced by in-situ powder metallurgy method. the produced powder mixtures were consolidated and sintered at optimum conditions. the resultant composites were solution treated at 495?c and aged at 170?c. the influence of graphite content on the bending strength of composites was studied. the distribution of graphite...
متن کاملRaney-nickel Catalysts Produced by Mechanical Alloying
Raney catalysts were prepared by a combination of mechanical alloying and leaching as an alternative in the synthesis of Raney-Nickel catalysts. Binary Al-Ni and ternary Al-Ni-Fe alloys with nominal compositions Al65Ni35, Al75Ni25, Al65Ni30Fe5, Al75Ni20Fe5 (in atomic percent), were processed from pure elemental powders; they consisted mainly of the intermetallic B2 AlNi phase. Aluminum was sele...
متن کاملInvestigation on Mechanical and Electrical Properties of Cu-Ti Nanocomposite Produced by Mechanical Alloying
In this paper, Cu-Ti nanocomposite synthesized via ball milling of copper-titanium powders in 1, 3, and 6 of weight percentage compounds. The vial speed was 350 rpm and ball to powder weight ratio kept at 15:1 under Argon atmosphere, and the time of milling was 90 h. Obtained powders were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS)....
متن کاملMechanical Properties and Wear Resistance of Sulfonated Graphene/Waterborne Polyurethane Composites Prepared by In Situ Method
In order to improve the dispensability of graphene oxide (GO) in waterborne polyurethane (WPU), sulfonated graphene (SGO) with superior dispersity was prepared by modifying graphene oxide with sodium 2-chloroethane sulfonate to introduce hydrophilic sulfonic groups into the structure. SGO/WPU composites were prepared using isophorone diisocyanate (IPDI), polytetramethylene ether glycol (PTMEG 2...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2016
ISSN: 2075-4701
DOI: 10.3390/met6020034