Wear Resistance of 304 Austenitic Stainless-steel Friction Welded Joints
نویسندگان
چکیده
منابع مشابه
Influence of rotational speed on the development of microstructure in a friction stir welded 304 austenitic stainless steel
Friction stir welding was conducted on AISI 304 austenitic stainless steel sheet with dimensions of 100 mm × 100 mm × 2 mm. The FSW was performed at a welding speed of 150 mm/min and rotational speeds of 400 and 800 rpm. The results showed that high frequency of low angle grain boundaries (LAGBs) were formed through dynamic recovery in the thermo-mechanically affected zone (TMAZ). Higher amoun...
متن کاملInfluence of rotational speed on the development of microstructure in a friction stir welded 304 austenitic stainless steel
Friction stir welding was conducted on AISI 304 austenitic stainless steel sheet with dimensions of 100 mm × 100 mm × 2 mm. The FSW was performed at a welding speed of 150 mm/min and rotational speeds of 400 and 800 rpm. The results showed that high frequency of low angle grain boundaries (LAGBs) were formed through dynamic recovery in the thermo-mechanically affected zone (TMAZ). Higher amoun...
متن کاملMicrostructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...
متن کاملSensitization Behavior of Gnaw Austenitic Stainless Steel Joints
The present work has been carried out to study the sensitization behavior of AISI 304L austenitic stainless steel weld, fabricated using GTAW (gas tungsten arc welding process). This weld was subjected to post weld thermal aging (PWTA) treatments lying in the sensitization range, viz. 700 ?C for 30 minutes, 500 minutes and 1000 minutes for studying the influence of carbide precipitation on thei...
متن کاملMicrostructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Journal of Duhok University
سال: 2020
ISSN: 1812-7568,2521-4861
DOI: 10.26682/csjuod.2020.23.1.20