Wettability between Nd2Fe14B and Nd-Rich Phase in Nd-Fe-B Alloy System
نویسندگان
چکیده
منابع مشابه
Nd-Fe-B Nanoparticles through Surfactant Assisted Mechanical Milling and Alloy Design
Surfactant-assisted mechanical milling has been used to produce discrete nanoparticles of both Nd-Fe-B and Sm-Co amenable for bottom-up production of nanostructured or nanocomposite permanent magnets. However, in Nd-Fe-B the comminution of the material proceeds by transgranular fracture, which influences both the morphology of the nanoparticles and the magnetic properties. This paper utilizes a...
متن کاملProduction of fine Nd-Fe-B alloy powder by pulsed plasma atomization
Extremely fine (<10 μm) Nd-Fe-B powder was generated by pulsed plasma atomization processing. The number average was just over 3 μm, as determined by computer-assisted scanning electron microscopy analysis of almost 3000 particles. Despite the fine particle size, alloys of stoichiometric Nd2Fe14B resulted in the properitectic formation of -Fe, deleteriously affecting the magnetic properties. N...
متن کاملCOERCIVITY AND THERMAL REMAGNETIZATION OF SINTERED Nd-Fe-B
Statistical methods are used to estimate coercivity J Hc and thermal remagnetization of uniaxially nucleationcontrolled permanent magnetic materials. Sintered Nd-Fe-B consists of the tetragonal magnetic Nd2FelrB phase with a volume fraction w = 80 % and of nonmagnetic phases. At temperatures above T, rz 150 K the tetragonal axis is the easy direction of magnetization [I]. It is well known [2] t...
متن کاملSintering of Nd-Fe-B Magnets from Dy Coated Powder
High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundar...
متن کاملHigh performance Nd-Fe-B permanent magnets without critical elements
Scanning electron microscopy, and magnetization measurements reveal that as cast (Nd1 xCex)2Fe14B alloys contain significant amounts of a-Fe that can be dramatically reduced by annealing the alloys at 1000 C for 3 days. The room temperature intrinsic coercivity, Hci, of (Nd0.8Ce0.2)2.2Fe14B melt spun ribbons was found to be 11 kOe, which is ~32e~10% higher in comparison to that of Nd2Fe14B (Hci...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals
سال: 2008
ISSN: 1880-6880,0021-4876
DOI: 10.2320/jinstmet.72.1010