evaluation of the effect of 2 flask investment materials on color stability of 5 brands of denture teeth
نویسندگان
چکیده
introduction: the purpose of this study was to investigate the effect of flask investment materials on the color changes of different brands of resin denture teeth. methods: resin denture teeth (560) were divided into 2 groups according to the materials used for flask investment (silicone or gypsum). all the specimens were thermocycled between 4°c and 60°c with 60-s dwell times for 1,000 cycles. subsequently, the specimens of each group were divided into 4 subgroups based on the immersion media: coffee, tea, cola, and distilled water. digital images of the teeth were taken before immersion and 30 days after immersion. the color samples were measured using the cie l*a*b* system, and color differences (∆e) were calculated. the data were evaluated by three ways anova and the tukey hsd test. results: there was not a significant difference in ∆e using three-way anova, while the results showed considerable statistical differences with two factor anova interaction. the ∆e values in the silicone group were significantly more than those in the gypsum group (p< 0.001). among the solutions in which specimens were kept, maximum discoloration was seen with coffee followed by cola, tea, and distilled water. the ivoclar vivadent denture teeth in the silicone group, as well as the apple teeth in the gypsum group exhibited the highest level of color stability. conclusion: all test groups exhibited visually perceptible color changes; the denture teeth and flask investment materials, as well as the nutritional habits, significantly affected the color stability of the resin denture teeth.
منابع مشابه
Evaluation of the Effect of 2 Flask Investment Materials on Color Stability of 5 Brands of Denture Teeth
Introduction: The purpose of this study was to investigate the effect of flask investment materials on the color changes of different brands of resin denture teeth. Methods: Resin denture teeth (560) were divided into 2 groups according to the materials used for flask investment (silicone or gypsum). All the specimens were thermocycled between 4°C and 60°C with 60-s dwell times for 1,000 cycles...
متن کاملhistological evaluation of the effect of three medicaments; trichloracetic acid, formocresol and mineral trioxide aggregate on pulpotomized teeth of dogs
چکیده ندارد.
15 صفحه اولthe effect of esp materials on medical studentsreading proficiency
چکیده این تحقیق " مواد درسی " را به عنوان یکی از بحث برانگیزترین موضوعات آموزش زبان تلقی کرده و درتلاش است به سه سوال عمده پاسخ دهد: 1) آیا بکارگیری جزوات گرداوری شده توسط گروهی از مدرسین تاثیر بسزایی در میزان توانش خواندن و درک متون انگلیسی دانشجویان پزشکی دارد؟ 2) آیا استفاده از مواد درسی اصلی( بین المللی )، توانش خواندن و درک متون انگلیسی دانشجویان پزشکی را به طور چشمگیری تحت تاثیر قرار م...
15 صفحه اولthe effect of explicit teaching of metacognitive vocabulary learning strategies on recall and retention of idioms
چکیده ندارد.
15 صفحه اولthe effect of authentic listening materials on the listening proficiency of efl learners in the intermediate level
having conducted the experiment and analysed the data, the researcher computed the groups mean scores and variances for the test relating to the research question. as the final atep, a t-test was conodonted for the hypothesis. as noted earlier, the significance level was determined at .05 and .01 respectively. the observed t-value was higher than the critical t-value at. 5 and .01 levels. conse...
15 صفحه اولthe effect of taftan pozzolan on the compressive strength of concrete in the environmental conditions of oman sea (chabahar port)
cement is an essential ingredient in the concrete buildings. for production of cement considerable amount of fossil fuel and electrical energy is consumed. on the other hand for generating one tone of portland cement, nearly one ton of carbon dioxide is released. it shows that 7 percent of the total released carbon dioxide in the world relates to the cement industry. considering ecological issu...
منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
journal of dental materials and techniquesجلد ۳، شماره ۴، صفحات ۱۴۴-۱۵۰
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023