convectional hydrothermal synthesis of high-purity pesudo-cubic bati0.09nb0.01o3 nanocrystals in rotary autoclave

نویسندگان

a. khanfekr

department of metallurgical and materials engineering, iran university of science and technology (iust), narmak, tehran, iran. m. tamizifar

department of metallurgical and materials engineering, iran university of science and technology (iust), narmak, tehran, iran. r. naghizadeh

department of metallurgical and materials engineering, iran university of science and technology (iust), narmak, tehran, iran.

چکیده

nano-sized batio3 powders with particular nb concentrations were prepared by rotary- hydrothermal (rh) method. hydrothermal method was used at 180 °c for 5 hours with new ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. new hydrothermal method was used instead of previous solid state reaction for the system batio3±nb2o3 in high temperature to achieve nano sized particles in lower time and temperature. synthesis with rotary-hydrothermal has the advantages of faster crystallization, decreased crystal size, more homogenous distribution of dopants at lower temperature and time in comparison with the solid state method. in case of the phase evolution studies the x-ray diffraction patterns (xrd) measurements and raman spectroscopy were performed. the transmission electron microscope (tem) and the field emission scanning electron microscopy (fe-sem) images were taken for the detailed analysis of the grain size, surface and morphology. synthesis of nb doped batio3 with the rotary- hydrothermal provided advantages of fast crystallization and decreased crystal size.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Convectional hydrothermal synthesis of high-purity pesudo-cubic BaTi0.09Nb0.01O3 nanocrystals in rotary autoclave

Nano-sized BaTiO3 powders with particular Nb concentrations were prepared by Rotary- Hydrothermal (RH) method. Hydrothermal method was used at 180 °C for 5 hours with new Ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. New hydrothermal method was used instead of previous solid state reaction for the system BaTiO3±Nb<sub...

متن کامل

Convectional hydrothermal synthesis of high-purity pesudo-cubic BaTi0.09Nb0.01O3 nanocrystals in rotary autoclave

Nano-sized BaTiO3 powders with particular Nb concentrations were prepared by Rotary- Hydrothermal (RH) method. Hydrothermal method was used at 180 °C for 5 hours with new Ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. New hydrothermal method was used instead of previous solid state reaction for the system BaTiO3±Nb<sub...

متن کامل

Microwave-Hydrothermal Synthesis and Characterization of High-Purity Nb Doped BaTiO3 Nanocrystals

The synthesis of Nb doped BaTiO3 has been investigated under Microwave-Hydrothermal (MH) conditions in the temperature of 150°C for only 2 h using C16H36O4Ti, BaH2O2.8H2O and NbCl5 as Ba, Ti and  Nb sources, respectively.  Typical experiments performed on MH processing have not yet reported for Nb doped BaTi...

متن کامل

microwave-hydrothermal synthesis and characterization of high-purity nb doped batio3 nanocrystals

the synthesis of nb doped batio3 has been investigated under microwave-hydrothermal (mh) conditions in the temperature of 150°c for only 2 h using c16h36o4ti, bah2o2.8h2o and nbcl5 as ba, ti and  nb sources, respectively.  typical experiments performed on mh processing have not yet reported for nb doped batio3.  in the mh process, the formation of high purity nano tetragonal nb-batio3 was stron...

متن کامل

Hydrothermal synthesis of monoclinic - cubic Li2TiO3 hybrid nanocomposite microspheres

Li2TiO3 compound is one of the most important tritium breeding ceramics for industrial application in the nuclear fusion reactor. The use of the hydrothermal method for preparing ceramic composite materials is new trend. In this work, hybrid nanocomposite microspheres of the nanocrystallites Li2TiO3 were prepared at low temperature 400°C. Nanocomposite powders synthesized by the batch supercrit...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of nano dimension

جلد ۶، شماره ۳، صفحات ۲۷۷-۲۸۱

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023