eco-friendly synthesis and characterization of ni-si nanoparticles mixed oxides as catalyst for

نویسندگان
چکیده

the nanoparticles of ni–si mixed oxides were prepared by co-precipitation method using nickel nitrate; ni(no3)2 6h2o and tetraethylorthosilicate (teos). the products were characterized by x-ray diffraction (xrd), transmission electron microscopy (tem), and hydrogen temperature program reduction (h2-tpr). the results revealed that ni–si mixed oxides particles were obtained with average particle size 1-2 nm. the ni-si nanoparticles mixed oxides successfully catalyzed the partial oxidation of methane (pom) to hydrogen and carbon monoxide (syn gas) using a fixed-bed reactor with about 92% activity and high selectivity. no coke formation and deactivation of catalyst were observed during the course of reaction. particularly significant is the similar reactivity of this catalyst with that of ni-ce-zr mixed oxides.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Eco-Friendly Synthesis and Characterization of Ni-Si Nanoparticles Mixed Oxides as Catalyst for

The nanoparticles of Ni–Si mixed oxides were prepared by co-precipitation method using nickel nitrate; Ni(NO3)2 6H2O and tetraethylorthosilicate (TEOS). The products were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), and hydrogen temperature program reduction (H2-TPR). The results revealed that Ni–Si mixed oxides particles were obtained with average particle ...

متن کامل

Synthesis of Binary Ti-Si Mixed Oxides Nanoparticles with Rutile Structure as Selective Catalyst for Epoxidation of Alkenes

The nanoparticles of Ti-Si mixed oxides (NTSO) with Rutile structure were prepared by sol-gel method in a mixture of alcohol and water as solvent. The solid product was characterized by XRD, FTIR, SEM, TEM, UV, TGA and laser Raman spectroscopy. The catalytic activity of NTSO (5-10 nm) was investigated in the epoxidation of cis stilbene, trans stilbene, and norbornene by using oxidants such as t...

متن کامل

synthesis of binary ti-si mixed oxides nanoparticles with rutile structure as selective catalyst for epoxidation of alkenes

the nanoparticles of ti-si mixed oxides (ntso) with rutile structure were prepared by sol-gel method in a mixture of alcohol and water as solvent. the solid product was characterized by xrd, ftir, sem, tem, uv, tga and laser raman spectroscopy. the catalytic activity of ntso (5-10 nm) was investigated in the epoxidation of cis stilbene, trans stilbene, and norbornene by using oxidants such as t...

متن کامل

Eco-friendly Synthesis of Magnesium Oxide Nanoparticles using Arabic Gum

Magnesium oxide nanoparticles were synthesized using Arabic gum as a biotemplate andmagnesium nitrate as the magnesium source by the sol-gel method. This method has manyadvantages such as nontoxic, economic viability, ease to scale up, less time consuming andenvironmental friendly approach for the synthesis of MgO nanoparticles without using anyorganic chemicals. Nanoparticles were characterize...

متن کامل

Synthesis and Characterization of V2O5/SiO2 Nanoparticles as Efficient Catalyst for Aromatization 1,4 Dihydropyridines

V2O5/SiO2 nanoparticles was prepared via an one-pot sol gel method from vanadyl- acetylacetonate and tetraethylorthosilicate in refluxing MeOH, followed by calcination at 700 °C for 2 hours. The resultant nanoparticles was characterized by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), TGA and FTIR techniques. Rapid and efficient ar...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of sciences islamic republic of iran

جلد ۲۰، شماره ۱، صفحات ۰-۰

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023