formation of a solid solution through accumulative roll bonding (arb) and post-heat treatment of multilayered cu/zn/al

نویسندگان

m. reihanian

m.m. mahdavian

l. ghalandari

a. obeidavi

چکیده

in the present study, the capability of accumulative roll bonding (arb) and subsequent heat-treatment to fabricate solid solution from a multilayered cu/zn/al was investigated. two post-heat treatment (one-step and two-step) routes were proposed. in the first, the arb processed material was heated to 800 c for 5:30 hours and allowed to cool slowly in a furnace (one-step route). in the second (two-step route), the composite was heated to 800 c for 3 hours and quenched in the cold water (0 ºc). the microstructures were characterized using a field emission scanning electron microscope (sem) equipped with energy dispersive x-ray detector (edx). the x-ray diffraction (xrd) pattern was used to identify the phases. results showed that even after imposing high arb cycles (up to 14 cycles), the solid solution could not be formed so far. however, after the subsequent heat-treatment, cu, zn and al distributed uniformly in the microstructure and a copper-based solid solution was formed.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Formation of a solid solution through accumulative roll bonding (ARB) and post-heat treatment of multilayered Cu/Zn/Al

In the present study, the capability of accumulative roll bonding (ARB) and subsequent heat-treatment to fabricate solid solution from a multilayered Cu/Zn/Al was investigated. Two post-heat treatment (one-step and two-step) routes were proposed. In the first, the ARB processed material was heated to 800 C for 5:30 hours and allowed to cool slowly in a furnace (one-step route). In the second (t...

متن کامل

Computational evaluation of the homogeneity of composites processed by accumulative roll bonding (ARB)

A new computational method based on MATLAB was used to study the effect of different parameters on the homogeneity of composites produced by a severe plastic deformation technique known as accumulative roll bonding. For a higher number of passes, the degree of particle agglomeration and clustering decreased, and an appreciable homogeneity was obtained in both longitudinal and transverse directi...

متن کامل

A Comparative Corrosion Study of Al/Al2O3-SiC Hybrid Composite Fabricated by Accumulative Roll Bonding (ARB)

In this study, the Al/Al2O3-SiC hybrid composite was produced by accumulative roll bonding (ARB). In the first and the second cycles, the particles were uniformly poured between the Al strips during each ARB cycle. In the subsequent cycles, ARB was repeated up to six cycles without adding the particles between the layers. After the total eight cycles, the particles were distributed uniformly wi...

متن کامل

INVESTIGATION OF TRIBOLOGICAL CHARACTERISTICS OF AL/NANO SiO2NANOCOMPOSITES PRODUCED BY ACCUMULATIVE ROLL BONDING (ARB) PROCESS

Accumulative roll-bonding process (ARB) is an important severe plastic deformation technique for production of the ultrafine grained, nanostructured and nanocomposite materials in the form of plates and sheets. In the present work, this process used for manufacturing Al/SiO 2 nanocomposites by using Aluminum 1050 alloy sheets and nano sized SiO 2 particles, at ambient temperature. After 8 cycle...

متن کامل

Ten years of severe plastic deformation (SPD) in Iran, part II: accumulative roll bonding (ARB)

The present paper is the second part of a previously published overview entitled “ten years of severe plastic deformation (SPD) in Iran”. Part I concentrates on the equal channel angular pressing (ECAP). In this part, the focus is on the accumulative roll bonding (ARB) because, currently, Iran is ranked the first in the world by the total number of publications in this field. In the present sec...

متن کامل

Corrosion Behavior of Al-2wt%Cu Alloy Processed By Accumulative Roll Bonding (ARB) Process

Accumulative roll bonding (ARB) imposes severe plastic strain on materials without changing the specimen dimensions. ARB process is mostly appropriate for practical applications because it can be performed readily by the conventional rolling process. An Al-2wt%Cu alloy was subjected to ARB process up to a strain of 4.8. Stacking of materials and conventional roll-bonding are repeated in the pro...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
iranian journal of materials forming

ناشر: shiraz university

ISSN

دوره 1

شماره 1 2014

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023