interaction between precipitation and dynamic recrystallization in hsla-100 microalloyed steel

نویسندگان

g. r. ebrahimi

a. momeni

h. eskandari

چکیده

strain induced precipitation in hsla-100 steel was investigated by conducting hotcompression and relaxation tests at temperature range of 850°c to 1100°c and strain rate of 0.001s-1 to 1s-1. the absence of dynamic recrystallization at temperatures below 1000°c was attributedto the influence of dynamic precipitation. the stress relaxation tests showed that strain inducedprecipitation is possible over a wide range of temperatures from 850°c to 1050°c. the startingand finishing times of precipitation were sensitive to temperature than strain rate. at temperaturerange of 950-1000°c and strain rate of 0.1s-1 the lowest times for precipitation were observed. thecombination of precipitation-time-temperature and recrystallization-time temperature diagramsshowed that at high temperatures and low strain rates, precipitation precedes dynamicrecrystallization, whereas at the opposite condition, dynamic recrystallization goes in advance. thestarting and finishing times for dynamic precipitation were approximated about 40 percent lowerthat those for strain induced precipitation.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Interaction Between Precipitation and Dynamic Recrystallization in HSLA-100 Microalloyed Steel

Strain induced precipitation in HSLA-100 steel was investigated by conducting hotcompression and relaxation tests at temperature range of 850°C to 1100°C and strain rate of 0.001s-1 to 1s-1. The absence of dynamic recrystallization at temperatures below 1000°C was attributedto the influence of dynamic precipitation. The stress relaxation tests showed that strain inducedprecipitation is possible...

متن کامل

Isothermal Recrystallization Behavior of Cold-deformed Martensite in an Ultra-low-carbon Microalloyed Steel

One of the most promising ways to produce a grain-refined microstructure in some steel materials is the thermomechanical processing route of subcritical recrystallization annealing of a cold-deformed martensite structure. In the present study, the microstructural evolutions and the associated recrystallization kinetics under various subcritical annealing heat treatment conditions are explored i...

متن کامل

Shear and tensile plastic behavior of austenitic steel TRIP-120 compared with martensitic steel HSLA-100

Themechanical performanceofTRIP-120, a novel transformation induced plasticity steel alloy, is evaluated for different loading cases and strain rates. The performance is compared with HSLA-100, a lowalloy steel developed by the United States Navy and currently used in naval hulls. The response of these materials under uniaxial tension and shear was investigated to the point of fracture at isoth...

متن کامل

Equilibrium Model of Precipitation in Microalloyed Steels

The formation of precipitates during thermal processing of microalloyed steels greatly influences their mechanical properties. Precipitation behavior varies with steel composition and temperature history and can lead to beneficial grain refinement or detrimental transverse surface cracks. This work presents an efficient computational model of equilibrium precipitation of oxides, sulfides, nitri...

متن کامل

Estimation of Maximum Inclusion Size and Fatigue Limit in HSLA-100 Steel

The objective of the current study is to determine the fatigue limit of a clean and high-performance material named as HSLA-100 steel and to compare the obtained fatigue limit with that of theoretically predicted fatigue limit by statistics of extreme value (SEV) method. Also, the size of inclusions located at the site of fatigue crack nucleation on the fracture surface of the fatigue test spec...

متن کامل

Dynamic Recrystallization and Hot Workability of 316LN Stainless Steel

Chaoyang Sun 1,*, Yu Xiang 1, Qingjun Zhou 2, Denis J. Politis 3, Zhihui Sun 1,* and Mengqi Wang 1 1 School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China; [email protected] (Y.X.); [email protected] (M.W.) 2 Capital Aerospace Machinery Company, Beijing 100076, China; [email protected] 3 Department of Mechanical Engineering, Imperial Co...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
iranian journal of materials forming

ناشر: shiraz university

ISSN

دوره 2

شماره 1 2015

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023