physical and mechanical features investigation of protein-based biodegradable films obtained from trout fish waste

نویسندگان

marziye mirzakhani

transfer phenomena laboratory (tpl), department of food science, technology and engineering, faculty of biosystems engineering, university of tehran sohrab moini

transfer phenomena laboratory (tpl), department of food science, technology and engineering, faculty of biosystems engineering, university of tehran zahra emam-djomeh

transfer phenomena laboratory (tpl), department of food science, technology and engineering, faculty of biosystems engineering, university of tehran

چکیده

biological packaging material based on obtained proteins from fish waste, are biopolymers that have the capability of biodegradable film formation. thus, purpose of this research is to study and investigate some of films’ physical features made from trout fish myofibril protein. the film forming solution containing 1.5%, 2% and 2.5%(w/v)myofibril protein isolate of 100ml solution and glycerol as plasticizer in three levels 25%, 50%, 75%(w/w) per dry material have been used. in order to solve existing protein in solution its ph must be reach to 3 by 1molar hcl. films have been produced by casting method for 48 hours in 25°c. then film’s mechanical features, water vapor penetrability, films solubility in water, transparency and color were investigated. effect of protein concentration was significantly obvious on films mechanical features, thickness, water vapor penetrability and color. obtained results from statistical analysis data by spss software showed that films with 2%(w/v) dry material along with 50%(w/w) glycerol demonstrated the best mechanical features.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Physical and mechanical features investigation of protein-based biodegradable films obtained from trout fish waste

Biological packaging material based on obtained proteins from fish waste, are biopolymers that have the capability of biodegradable film formation. Thus, purpose of this research is to study and investigate some of films’ physical features made from trout fish Myofibril protein. The film forming solution containing 1.5%, 2% and 2.5%(w/v)Myofibril protein isolate of 100ml solution and glycerol a...

متن کامل

Physical and mechanical features investigation of protein-based biodegradable films obtained from trout fish waste

Biological packaging material based on obtained proteins from fish waste, are biopolymers that have the capability of biodegradable film formation. Thus, purpose of this research is to study and investigate some of films’ physical features made from trout fish Myofibril protein. The film forming solution containing 1.5%, 2% and 2.5%(w/v) Myofibril protein isolate of 100ml solution and glycerol ...

متن کامل

Physical and mechanical features investigation of protein-based biodegradable films obtained from trout fish waste

Biological packaging material based on obtained proteins from fish waste, are biopolymers that have the capability of biodegradable film formation. Thus, purpose of this research is to study and investigate some of films’ physical features made from trout fish Myofibril protein. The film forming solution containing 1.5%, 2% and 2.5% (w/v) Myofibril protein isolate of 100ml solution and glycerol...

متن کامل

determination of some physical and mechanical properties red bean

چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...

15 صفحه اول

physical and mechanical properties of biodegradable edible film obtained from salep

in this study the feasibility of using salep as a new film-forming material was studied. the mechanical properties, water vapor permeability and thickness of salep films incorporated with glycerol were determined. increasing the content of dry material of salep from 1% to 3%(w/v) increased values for tensile strength and elongation at break from 16.16% and 18.85 mpa to 70.15% and 24.50 mpa resp...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of food and bioprocess engineering

جلد ۱، شماره ۲، صفحات ۵۵-۶۸