fabrication of ultrathin graphene oxide-coated membrane with hydrophilic properties for arsenate removal from water

نویسندگان

reza rezaee

environmental health research center, kurdistan university of medical sciences, sanandaj, iran simin nasseri

center for water quality research (cwqr), institute for environmental research (ier), tehran university of medical sciences, tehran, iran amir hossein mahvi

department of environmental health engineering, school of public health, tehran university of medical sciences, tehran, iran ali jafari

department of environmental health engineering, faculty of health and nutrition, lorestan university of medical sciences, khorramabad, iran mahdi safari

چکیده

terms and conditions of current drinking water quality standards, including reducing the maximum arsenic concentration from 50 μgl-1 to 10 μgl-1 and predicted stricter standards in future, reveals the necessity for development of new technologies. this study aimed to prepare and evaluate a new nanocomposite membrane using graphene oxide (go) thin layer to remove arsenic (v) from water. to fabricate the membrane, initially go was prepared using the modified hummers' method and then to gain a narrow-dispersed go dispersion, several times centrifugation and sonication were performed. then resultant dispersed go was coated on a microporous flat-sheet polyethersulfone support by coating/deposition and vacuum filtration process. performance of the synthesized membrane was assessed using a dead end filtration system. the results showed that pure water flux decreased as the coated go thickness increased. among the three prepared membranes, the greatest flux was attributed to m1 membrane with the value of 398.5 lm-2h-1 and the minimum flux was for m3 with a value of 131.3 lm-2h-1 at 4 bar of pressure. furthermore, by increasing the coated go, rejection of arsenate ions increased significantly. with initial concentration of 1000 ± 20 μgl-1, percentage of arsenate rejection for m1, m2 and m3 membranes were 41.8%, 73.5% and 86.7%, respectively. relatively high removal by this novel membrane can be due to the exceptional properties of go nanostructure and the presence of hydrophilic functional groups.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Fabrication of ultrathin graphene oxide-coated membrane with hydrophilic properties for arsenate removal from water

Terms and conditions of current drinking water quality standards, including reducing the maximum arsenic concentration from 50 μgl-1 to 10 μgl-1 and predicted stricter standards in future, reveals the necessity for development of new technologies. This study aimed to prepare and evaluate a new nanocomposite membrane using graphene oxide (GO) thin layer to remove arsenic (v) from water. To fabri...

متن کامل

Fabrication and characterization of a polysulfone-graphene oxide nanocomposite membrane for arsenate rejection from water

BACKGROUND Nowadays, study and application of modified membranes for water treatment have been considered significantly. The aim of this study was to prepare and characterize a polysulfone (PSF)/graphene oxide (GO) nanocomposite membrane and to evaluate for arsenate rejection from water. MATERIALS AND METHODS The nanocomposite PSF/GO membrane was fabricated using wet phase inversion method. T...

متن کامل

Dye removal from water by zinc ferrite-graphene oxide nanocomposite

In this work, zinc ferrite magnetic and zinc ferrite-graphene oxide nanocomposite were synthesized through a facile hydrothermal method and dye removal capability as an adsorbent were studied. Fourier transform infrared spectroscopy FT-IR, X-ray diffraction XRD and scanning electron microscopy SEM were used to characterize the synthesized nanocomposite. The UV-Vis results showed that the additi...

متن کامل

Enhanced removal performance of arsenate and arsenite by magnetic graphene oxide with high iron oxide loading.

Magnetic iron oxide/graphene oxide (MGO) with high iron loading (51 wt%) has been successfully synthesized using the co-precipitation method, and then used as adsorbents for the removal of arsenate and arsenite from aqueous solutions. The resulting MGO possesses desirable magnetic properties (12.8 emu g(-1)) and excellent adsorption properties for the removal of As(III) and As(IV) with signific...

متن کامل

Removal of Fe2+ from Aqueous Solution Using Manganese Oxide Coated Zeolite and Iron Oxide Coated Zeolite

The adsorption of Fe2+ by the manganese oxide coated zeolite (MOCZ) and iron oxide coated zeolite (FOCZ) was studied. Surface properties of adsorbents have been investigated for monitoring their changes and morphology for both of the MOCZ and FOCZ. Main variables namely; contact time, pH, initial concentration of Fe2+, size and dosage of adsorbent have been optimized, and the results contrasted...

متن کامل

XANES evidence of arsenate removal from water with magnetic ferrite.

Arsenic (As) in groundwater and surface water is a worldwide problem possessing a serious threat to public health. In this study, a magnetic ferrite, was synthesized and investigated for its As(V) removal efficiency. The adsorption of As(V) by magnetic ferrite exhibited an L-shaped nonlinear isotherm, suggesting limiting binding sites on the adsorbent surface. The As K-edge X-Ray Absorption Nea...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of advances in environmental health research

جلد ۴، شماره ۳، صفحات ۱۶۹-۱۷۵

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023