electrochemical and tribological behaviour of oxide dispersion strengthened duplex stainless steel in mine water environment

نویسندگان

oladayo olaniran

metallurgical & materials engineering federal university of technology, pmb 704, akure, ondo state, nigeria

چکیده

abstract this work investigated the electrochemical and aqueous tribological behavior of hot pressed 2205 duplex stainless steel (dss). dss sintered composites of different volume percent (% vol) of partially stabilized zirconia (psz) was developed using powder metallurgy (pm) technique. electrochemical behaviour was studied at room temperature, using open circuit potential and potentiodynamic scanning in simulated mine water and 3.5% nacl solution while aqueous tribological test was carried out in simulated mine water. the influence of psz, cr and ni additions on the degradation mechanisms of corrosion and wear of the modified dss were evaluated. x-ray microtomography (xrm) was used as experimental technique for defect analysis from the corrosion studies. results show the surface imaging capability of sem and the internal structures imaging capability of xrm. sem revealed important surface degradation mechanisms of the materials whilst relevant information on pitting corrosion was obtained from xrm. it was deduced that, pitting corrosion can be caused by the growth of intergranular corrosion resulting from the attack and the breakdown of passive films by chloride ions which affected both the surface and the internal parts of the samples.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Electrochemical and Tribological Behaviour of Oxide Dispersion Strengthened Duplex Stainless Steel in Mine Water Environment

Abstract This work investigated the electrochemical and aqueous tribological behavior of hot pressed 2205 duplex stainless steel (DSS). DSS sintered composites of different volume percent (% vol) of partially stabilized zirconia (PSZ) was developed using powder metallurgy (PM) technique. Electrochemical behaviour was studied at room temperature, using open circuit potential and potentiody...

متن کامل

Surface Texturing-Plasma Nitriding Duplex Treatment for Improving Tribological Performance of AISI 316 Stainless Steel

Surface texturing-plasma nitriding duplex treatment was conducted on AISI 316 stainless steel to improve its tribological performance. Tribological behaviors of ground 316 substrates, plasma-nitrided 316 (PN-316), surface-textured 316 (ST-316), and duplex-treated 316 (DT-316) in air and under grease lubrication were investigated using a pin-on-disc rotary tribometer against counterparts of high...

متن کامل

ELECTROCHEMICAL BEHAVIOUR OF AISI 304 STAINLESS STEEL IN SULFURIC SOLUTION: EFFECTS OF ACID CONCENTRATION

The effects of H2SO4 concentration on the electrochemical behaviour of passive films formed on AISI 304 stainless steel were investigated using by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Potentiodynamic polarization indicated that the corrosion potentials were found to shift towards negative direction with an increase in solution co...

متن کامل

Microstructure, Mechanical and Tribological Properties of Oxide Dispersion Strengthened High-Entropy Alloys

A novel metal matrix composite CrMnFeCoNi with Y₂O₃ as reinforcement phase was designed and manufactured by mechanical alloying and spark plasma sintering. After sintering at 900 °C for 5 min, the microstructure consisted of a FCC matrix and Y₂O₃ nanoparticles. The addition of 0.25 wt % Y₂O₃ increased the room temperature tensile strength of the CrMnFeCoNi base from 868 MPa to 1001 MPa, while t...

متن کامل

Water Lubrication of Stainless Steel using Reduced Graphene Oxide Coating

Lubrication of mechanical systems using water instead of conventional oil lubricants is extremely attractive from the view of resource conservation and environmental protection. However, insufficient film thickness of water due to low viscosity and chemical reaction of water with metallic materials have been a great obstacle in utilization of water as an effective lubricant. Herein, the frictio...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of advanced materials and processing

جلد ۵، شماره ۱، صفحات ۵۷-۶۸

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023