relationship between cell compatibility and elastic modulus of silicone rubber/organoclay nanobiocomposites

background substrates in medical science are hydrophilic polymers undergoing volume expansion when exposed to culture medium that influenced on cell attachment. although crosslinking by chemical agents could reduce water uptake and promote mechanical properties, these networks would release crosslinking agents. in order to overcome this weakness, silicone rubber is used and reinforced by nanoclay. objectives attempts have been made to prepare nanocomposites based on medical grade htv silicone rubber (sr) and organo-modified montmorillonite (ommt) nanoclay with varying amounts of clay compositions. materials and methods incorporation of nanocilica platelets into sr matrix was carried out via melt mixing process taking advantage of a brabender internal mixer. the tensile elastic modulus of nanocomposites was measured by performing tensile tests on the samples. produced polydimetylsiloxane (pdms) composites with different flexibilities and crosslink densities were employed as substrates to investigate biocompatibility, cell compaction, and differential behaviors. results the results presented here revealed successful nanocomposite formation with sr and ommt, resulting in strong pdms-based materials. the results showed that viability, proliferation, and spreading of cells are governed by elastic modulus and stiffness of samples. furthermore, adipose derived stem cells (adscs) cultured on pdms and corresponding nanocomposites could retain differentiation potential of osteocytes in response to soluble factors, indicating that inclusion of ommt would not prevent osteogenic differentiation. moreover, better spread out and proliferation of cells was observed in nanocomposite samples. conclusions considering cell behavior and mechanical properties of nanobiocomposites it could be concluded that silicone rubber substrate filled by nanoclay are a good choice for further experiments in tissue engineering and medical regeneration due to its cell compatibility and differentiation capacity.