kinetics of sphalerite leaching by sodium nitrate in sulfuric acid

نویسندگان

m. hasani

seyed m. j. koleini

a. khodadadi

چکیده

in the present work, the extraction of zinc from a sphalerite concentrate using sodium nitrate as an oxidant in a sulfuric acid solution was investigated. the effective parameters such as the temperature, sulfuric acid and sodium nitrite concentrations, stirring speed, particle size, and solid/liquid (s/l) ratio were analyzed. the dissolution rate increased with increase in the sulfuric acid and sodium nitrite concentrations and temperature but decreased with increase in the particle size and s/l ratio. moreover, the stirring speed had a significant effect on the leaching rate. under the optimum conditions, 74.11% of zinc was obtained. the kinetic data obtained was analyzed by the shrinking core model (scm). a new scm variant captured the kinetic data more appropriately. based on this model, the activities of the reactants control the diffusion but the two concentrations affect the second order reaction rate or diffusion in both directions. at 75 ˚c, the r2 values in the surface chemical reactions and diffusion were 0.78 and 0.89, respectively. using the new model, however, the r2 value 0.989 was obtained. the reaction orders with respect to [h2so4], [nano3], s/l ratio, and particle size were 1.603, 1.093, ‒0.9156, and ‒2.177, respectively. the activation energy for the dissolution was 29.23 kj/mol.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Kinetics of Sphalerite Leaching by Sodium Nitrate in Sulfuric Acid

In the present work, the extraction of zinc from a sphalerite concentrate using sodium nitrate as an oxidant in a sulfuric acid solution was investigated. The effective parameters such as the temperature, sulfuric acid and sodium nitrite concentrations, stirring speed, particle size, and solid/liquid (S/L) ratio were analyzed. The dissolution rate increased with increase in the sulfuric acid an...

متن کامل

Kinetics of Sphalerite leaching by Sodium Nitrate in Sulfuric Acid

In the present work, the extraction of zinc from a sphalerite concentrate using sodium nitrate as an oxidant in a sulfuric acid solution was investigated. The effective parameters such as the temperature, sulfuric acid and sodium nitrite concentrations, stirring speed, particle size, and solid/liquid (S/L) ratio were analyzed. The dissolution rate increased with increase in the sulfuric acid an...

متن کامل

Kinetics and Mechanism of Sphalerite Leaching by Sodium Nitrate in Sulphuric Acid Solution

Interest for application of hydrometallurgical processes in a processing of complex sulphide ores and concentrates has increased in recent years. Their application provides better metal recoveries and reduced emission of gaseous and toxic ageneses in the environment. The kinetics and mechanism of sphalerite leaching from complex sulphide concentrate with sulphuric acid and sodium nitrate soluti...

متن کامل

Leaching Kinetics of Stibnite in Sodium Hydroxide

Spherical pellets of antimony sulphide were dissolved in 1 molar sodium hydroxide solutions at different temperatures. It was found that the shrinking core with ash layer model could satisfactorily explain the dissolution process. Using this model it was found that initially the rate controlling step is a chemical reaction with activation energy of 10.2 kJ/mol. As the ash layer builds up, diffu...

متن کامل

THE LEACHING OF NEZAMABAD SCHEELITE WITH SULFURIC ACID

A new process for recovering scheelite ores comprises producing a concentrate from the ore, then leaching the concentrate with H_2SO_4 in the presence of H_3PO_4 and Na Cl at atmosphericpressure are discussed. Finely purification of the product will be described. The amounts of dissolution of tungsten in acid depend on the parameters such as time, temperature, type and concentration of acid an...

متن کامل

Leaching Kinetics of Zinc from Metal Oxide Varistors (MOVs) with Sulfuric Acid

Abstract: The leaching kinetics of zinc from zinc oxide-based metal oxide varistors (MOVs) was investigated in H2SO4 at atmospheric pressure. Kinetics experiments were carried out at various agitation speeds, particle sizes, initial H2SO4 concentrations, and reaction temperatures. It was determined that the leaching rate of zinc was independent of agitation speed above 300 rpm and also independ...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of mining and environment

ناشر: university of shahrood

ISSN 2251-8592

دوره 7

شماره 1 2016

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023