sono-chemical synthesis fe3o4-mg(oh)2 nanocomposite and its photo-catalyst investigation in methyl orange degradation

نویسندگان

g. nabiyouni

d. ghanbari

s. karimzadeh

b. samani ghalehtaki

چکیده

in this work firstly fe3o4 nanoparticles were synthesized via a sono-chemical method. at the second step magnesium hydroxide shell was synthesized on the magnetite-core under ultrasonic waves. for preparation fe3o4-mgo the product was calcinated at 400 ºc for 2h. properties of the product were examined by x-ray diffraction pattern (xrd), scanning electron microscope (sem) and fourier transform infrared (ft-ir) spectroscopy. vibrating sample magnetometer (vsm) shows nanoparticles exhibit super-paramagnetic behavior. the photo-catalytic behavior of fe3o4-mg(oh)2  nanocomposite was evaluated using the degradation of a methyl orange (meo) aqueous solution under ultraviolet (uv) light irradiation. the results show that fe3o4-mg(oh)2 nanocomposites have applicable magnetic and photo-catalytic performance.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Sono-chemical Synthesis Fe3O4-Mg(OH)2 Nanocomposite and Its Photo-catalyst Investigation in Methyl Orange Degradation

In this work firstly Fe3O4 nanoparticles were synthesized via a sono-chemical method. At the second step magnesium hydroxide shell was synthesized on the magnetite-core under ultrasonic waves. For preparation Fe3O4-MgO the product was calcinated at 400 ºC for 2h. Properties of the product were examined by X-ray diffraction pattern (XRD), scanning electron microscope (SEM) and Fourier transform ...

متن کامل

Microwave-assisted Synthesis of MgFe2O4-ZnO Nanocomposite and Its Photo-catalyst Investigation in Methyl Orange Degradation

In this work firstly MgFe2O4 nanoparticles were synthesized via a microwave-assisted method. The product was calcinated at 900 ºC for 2h. At the second step zinc oxide shell was synthesized on the ferrite under ultrasonic waves. Properties of the product were examined by X-ray diffraction pattern (XRD), scanning electron microscope (SEM) and Fourier transform infrared (FT-IR) spectroscopy. Vibr...

متن کامل

microwave-assisted synthesis of mgfe2o4-zno nanocomposite and its photo-catalyst investigation in methyl orange degradation

in this work firstly mgfe2o4 nanoparticles were synthesized via a microwave-assisted method. the product was calcinated at 900 ºc for 2h. at the second step zinc oxide shell was synthesized on the ferrite under ultrasonic waves. properties of the product were examined by x-ray diffraction pattern (xrd), scanning electron microscope (sem) and fourier transform infrared (ft-ir) spectroscopy. vibr...

متن کامل

Synthesis, characterization and degradation activity of Methyl orange Azo dye using synthesized CuO/α-Fe2O3 nanocomposite

This study investigated the photo-degradation of methyl orange (MO) as a type of azo dye using a CuO/α-Fe2O3 nanocomposite. A CuO/α-Fe2O3 powder with a crystalline size in the range of 27-49 nm was successfully prepared using simple co-precipitation along with a sonication method. The characterization of the synthesized sample was done via XRD, FE-SEM, EDS, FTIR and DRS analyses. The Tauc equat...

متن کامل

Synthesis of Magnesium Ferrite-Silver Nanostructures and Investigation of its Photo-catalyst and Magnetic Properties

In this research we first synthesized MgFe2O4 nanostructures via hydrothermal method using (Mg(NO₃)₂.6H₂O) and (Fe(NO₃)₃.9H₂O). The influence of concentration, surfactant, precipitating agent and temperature on the particle size and magnetic properties of the synthesised nanoparticles were examined. Then MgFe2O4-Ag nanocomposites were prepared by a simple chemical precipitation. The structural ...

متن کامل

Sol-gel Synthesis of ZnO Nanoparticles and ZnO-TiO2-SiO2 Nanocomposites and Their Photo-catalyst Investigation in Methylene Blue Degradation

In this work firstly ZnO nanoparticles were synthesized via a simple precipitation method. At the second step titanium dioxide and silicon dioxide shell were synthesized on the core. For preparation ZnO-TiO2-SiO2 the sol product was calcinated at 500 ºC for 2h. Properties of the product were examined by X-raydiffraction pattern (XRD), scanning electron microscope (SEM) and Fourier transform inf...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of nanostructures

ناشر: university of kashan

ISSN 2251-7871

دوره 4

شماره 4 2014

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023