growth defects and chromium content loss during the deposition of stainless steel by cae-pvd and its effect on the corrosion and passivation behavior of the coating

نویسندگان

a. sanati

k. raeissi

h. edris

چکیده

in the present study, the effects of growth defects and chromium content loss on the degradation of corrosion andpassivation of cathodic arc evaporation (cae-pvd) of stainless steel coating were investigated in 2 m sulphuricacid solution. eds analysis indicated that the micro-particles were obtained during the coating growth. in addition,it was detected that the growth defects had poor adhesion to the coating matrix and in the open circuit potential(ocp), they were detached from the coating, providing appropriate conditions for the penetration of the solution.in addition, loss of chromium during evaporation was found to be detrimental to the passivation of the stainlesssteel coating and the formation of a porous oxide layer. the average percent of the main elements of the coating,according to eds area analysis, was fe-13cr-6ni. moreover, the lower semicircle diameter of the coating inelectrochemical impedance spectroscopy (eis) measurements revealed the lower polarization resistance of it, incomparison to that of the bulk 304 stainless steel.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Growth Defects and Chromium Content Loss during the Deposition of Stainless Steel by CAE-PVD and Its Effect on the Corrosion and Passivation Behavior of the Coating

In the present study, the effects of growth defects and chromium content loss on the degradation of corrosion and passivation of cathodic arc evaporation (CAE-PVD) of stainless steel coating were investigated in 2 M sulphuric acid solution. EDS analysis indicated that the micro-particles were obtained during the coating growth. In addition, it was detected that the growth defects had poor adhes...

متن کامل

the survey of the virtual higher education in iran and the ways of its development and improvement

این پژوهش با هدف "بررسی وضعیت موجود آموزش عالی مجازی در ایران و راههای توسعه و ارتقای آن " و با روش توصیفی-تحلیلی و پیمایشی صورت پذیرفته است. بررسی اسنادو مدارک موجود در زمینه آموزش مجازی نشان داد تعداد دانشجویان و مقاطع تحصیلی و رشته محل های دوره های الکترونیکی چندان مطلوب نبوده و از نظر کیفی نیز وضعیت شاخص خدمات آموزشی اساتید و وضعیت شبکه اینترنت در محیط آموزش مجازی نامطلوب است.

the effect of functional/notional approach on the proficiency level of efl learners and its evaluation through functional test

in fact, this study focused on the following questions: 1. is there any difference between the effect of functional/notional approach and the structural approaches to language teaching on the proficiency test of efl learners? 2. can a rather innovative language test referred to as "functional test" ge devised so so to measure the proficiency test of efl learners, and thus be as much reliable an...

15 صفحه اول

the washback effect of discretepoint vs. integrative tests on the retention of content in knowledge tests

در این پایان نامه تاثیر دو نوع تست جزیی نگر و کلی نگر بر به یادسپاری محتوا ارزیابی شده که نتایج نشان دهندهکارایی تستهای کلی نگر بیشتر از سایر آزمونها است

15 صفحه اول

the study of practical and theoretical foundation of credit risk and its coverage

پس از بررسی هر کدام از فاکتورهای نوع صنعت, نوع ضمانت نامه, نرخ بهره , نرخ تورم, ریسک اعتباری کشورها, کارمزد, ریکاوری, gdp, پوشش و وثیقه بر ریسک اعتباری صندوق ضمانت صادرات ایران مشخص گردید که همه فاکتورها به استثنای ریسک اعتباری کشورها و کارمزد بقیه فاکتورها رابطه معناداری با ریسک اعتباری دارند در ضمن نرخ بهره , نرخ تورم, ریکاوری, و نوع صنعت و ریسک کشورها اثر عکس روی ریسک اعتباری داردو پوشش, وثی...

15 صفحه اول

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of iron & steel society of iran

ناشر: iron & steel society of iran

ISSN 1735-4145

دوره 12

شماره 2 2015

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023