effect of combining hydraulic and phosphate bonds on alumina-spinel low cement castables

نویسندگان

m. paghandeh

a. monshi

r. emadi

چکیده

a basic alumina-spinel low cement castable (lcc) composed of sintered bauxite, reactive alumina, calcined alumina, calcined magnesia, microsilica, and high alumina refractory cement was prepared (castable a) to which 5% sodium hexa-meta phosphate was later added (castable b) to prepare samples for heat treatment at 110ºc, 900ºc, and 1400ºc. bulk density (bd), apparent porosity (ap), and cold crushing strength (ccs) were measured and xrd and sem studies were performed. it was shown that after heat treating at 110ºc, ccs of castable b increased by more than 3 times while its ap value was less than half that of castable a. the main difference between the two samples was found to lie in the presence of mg2p2o7 and alpo4.2h2o which are responsible for increases in ccs. at the temperature range of 800-1000ºc where the hydraulic bond reverses to the dehydrated condition and castable a becomes weak with high porosity, castable b showed a ccs value of more than 4 times. needles of magnesium phosphate were found to be responsible for reinforcing the microstructure of castable b at 900ºc. after firing at 1400ºc, castable b showed extraordinary ccs values of up 100 mpa (about 1000 kg/cm2), 5 times stronger, and ap% of below 1/5 times that of castable a. the phases present after firing were alumina, al2o3, spinel, mgal2o4, calcium phosphate, ca3 (po4)2 and enstatite, and mgsio3. magnesium phosphate melted at 1300-1400ºc and aided the formation of ceramic bonds. the ca coming from calcium aluminate cement reacted with phosphate and developed refractory calcium phosphate.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of Combining Hydraulic and Phosphate Bonds on Alumina-Spinel Low Cement Castables

A basic alumina-spinel low cement castable (LCC) composed of sintered bauxite, reactive alumina, calcined alumina, calcined magnesia, microsilica, and high alumina refractory cement was prepared (castable A) to which 5% sodium hexa-meta phosphate was later added (castable B) to prepare samples for heat treatment at 110ºC, 900ºC, and 1400ºC. Bulk Density (BD), Apparent Porosity (AP), and Cold Cr...

متن کامل

INFLUENCE OF NANO SILICA ON PROPERTIES AND MICROSTRUCTURE OF HIGH ALUMINA ULTRA-LOW CEMENT REFRACTORY CASTABLES

Colloidal silica bonded refractory castables have been developed recently. It was found that colloidal silica is one of the best binders can substitute other binders such as cement in No Cement Castable (NCC) and Ultra Low Cement Castable (ULCC) refractories. Also composition of colloidal silica with appropriate additives resulted in a gel form which makes the initial strength. Moreover, the na...

متن کامل

effect of seed priming and irrigation regimes on yield,yield components and quality of safflowers cultivars

این مطالعه در سال 1386-87 در آزمایشگاه و مزرعه پژوهشی دانشگاه صنعتی اصفهان به منظور تعیین مناسب ترین تیمار بذری و ارزیابی اثر پرایمینگ بر روی سه رقم گلرنگ تحت سه رژیم آبیاری انجام گرفت. برخی از مطالعات اثرات سودمند پرایمینگ بذر را بر روی گیاهان مختلف بررسی کرده اند اما در حال حاضر اطلاعات کمی در مورد خصوصیات مربوط به جوانه زنی، مراحل نموی، عملکرد و خصوصیات کمی و کیفی بذور تیمار شده ژنوتیپ های م...

Investigation of the Effect of high Alumina Cement on the Properties of Foamed Alumina Insulation Bricks

The purpose of this study was to investigate the effect of high alumina cement and Sintering temperature on microstructure, physical and mechanical properties of foamed alumina insulation bricks. The Slurry samples  were prepared containing 75wt% of alumina and 25% wt of deionised water containing 1%, 3%, 5%, 7% wt% high Alumina cement and 2% wt% foam. Then samples were poured into metal molds....

متن کامل

Densification characteristics of chromia/alumina castables by particle size distribution

The quality of the refractories applied on integrated gasification combined cycle should be a key factor that affects both the reliability and the economics of gasifier operation. To enhance the workability of chromia/alumina castables, three types of ultrafine alumina powder were added to improve the workability. Densification behavior of such castables in the presence of ultrafine alumina was...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of iron & steel society of iran

ناشر: iron & steel society of iran

ISSN 1735-4145

دوره 5

شماره 1 2008

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023