developing very fine nanopearlitic structure in a high carbon steel wire before drawing

نویسندگان

s. sadeghpour

چکیده

the effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. in this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. the results were the minimum interlamellar spacing of 35 nm and maximum ultimate strength of 1960 mpa for austenitizing at 910 ˚c and isothermally transforming to pearlite at 510 ˚c.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Developing Very Fine Nanopearlitic Structure in a High Carbon Steel Wire before Drawing

The effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. In this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. The results were the minimum interlamellar spacing of 35 nm and maximum ulti...

متن کامل

The Influence of Drawing Speed on Structure Changes in High Carbon Steel Wires

M. Suliga, R. Kruzel, T. Garstka, Czestochowa University of Technology, Czestochowa, Poland J. Gazdowicz Institute of Ferrous Metallurgy Gliwice, Poland In the paper the influence of the drawing speed on structure changes has been assessed. The Scanning Electron Microscope investigation confirmed that for wires drawn with high total draft, exceeding 80 %, makes it impossible to clearly assess t...

متن کامل

Carbon dioxide concentrations are very high in developing oilseeds.

A new method has been developed to rapidly determine the total inorganic carbon concentration (gaseous [CO2] + aqueous [CO(2)] + [HCO3-] + [CO3(2)-]) in developing seeds. Seeds are rapidly dissected and homogenized in 1 N HCl in gas-tight vials. The headspace gas is then analyzed by infrared gas analysis. Developing rapeseed (Brassica napus L.) and soybean [Glycine max (L.) Merr.] seeds were an...

متن کامل

Static Strain Aging Behavior of Low Carbon Steel Drawn Wire

The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...

متن کامل

Recrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant

In the present work the recrystallization behavior of deep drawing grade Al-killed low carbon steel sheets produced by Mobarakeh Steel Plant (MSP) has been studied. Salt bath isothermal annealing has b...

متن کامل

Progressive Changes in the Microstructure and Texture in Pearlitic Steel during Wire Drawing

The evolution of microstructure and texture during wire drawing of pearlitic steel was studied using scanning electron microscopy and X-ray diffraction. Wire drawing induces elongation of ferrite grains with the development of <110> fibre texture. The cementite lamellae also have a tendency to reorient themselves along the wire axis with increasing strain. Viscoplastic self-consistent simulatio...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of iron & steel society of iran

ناشر: iron & steel society of iran

ISSN 1735-4145

دوره 8

شماره 2 2011

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023