Comparison of AH26 Physicochemical Properties with Two AH26/Antibiotic Combinations

INTRODUCTION The purpose of this study was to compare the setting time and post-setting solubility, flow, film thickness and dimensional changes of AH26 root canal sealer with AH26-Antibiotic combination. MATERIALS AND METHODS This study was performed according to British standard BS 6876 (2001) which tests the physicochemical properties of endodontic sealers. Three samples of each of tested materials including AH26 alone, AH26/amoxicillin and AH26/doxycycline were used to test each of the properties. They were prepared according to ISO protocols. RESULTS The setting time of studied materials was 46 hours for AH26, 29 hours for AH26/amoxicillin, 49 hours for AH26/doxycycline. Flow test results were as follows, for AH 26, 15.6 mm; AH26/amoxicillin, 14.9 mm; AH26/doxycycline, 14.2 mm. Film thickness was 0.024 mm in AH26, 0.0283 mm in AH26/amoxicillin, 0.0276 mm AH26/doxycycline. The solubility of AH26 was 0.0076%, AH26/amoxicillin, 0.0113%, and for AH26/doxycycline, 0.013 %. Dimensional changes following setting was 0.07 mm, 2.6 mm, and 1.1 mm for AH 26, AH26/amoxicillin, and AH26/doxycycline, respectively. CONCLUSION The physico-mechanical properties of AH26 antibiotic combinations were superior compared with AH26, with the exception of flow. Also, AH26/amoxicillin had a lower setting time than AH26. However, all values were within an acceptable range which conformed to ISO.