Growth and characterization of aligned carbon nanotubes from patterned nickel nanodots and uniform thin films

نویسندگان

  • J. G. Wen
  • Z. P. Huang
  • D. Z. Wang
  • J. H. Chen
  • S. X. Yang
  • Z. F. Ren
  • J. H. Wang
چکیده

Microstructures of well-aligned multiwall carbon nanotubes grown on patterned nickel nanodots and uniform thin films by plasma-enhanced chemical vapor deposition have been studied by electron microscopy. It was found that growth of carbon nanotubes on patterned nickel nanodots and uniform thin films is different. During growth of carbon nanotubes, a nickel particle sits at the tip of each nanotube, and its [220] is preferentially oriented along the plasma direction, which can be explained by a channeling effect of ions coming into nickel particles in plasma. The alignment of nanotubes is induced by the electrical field direction relative to substrate surface.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Optimized Conditions for Catalytic Chemical Vapor Deposition of Vertically Aligned Carbon Nanotubes

Here, we have synthesized vertically aligned carbon nanotubes (VA-CNTs), using chemical vapor deposition (CVD) method. Cobalt and ethanol are used as the catalyst and the carbon source, respectively. The effects of ethanol flow rate, thickness of Co catalyst film, and growth time on the properties of the carbon nanotube growth are investigated. The results show that the flow rate of ethanol and...

متن کامل

Role of growth temperature in CVD synthesis of Carbon nanotubes from Ni-Co bimetallic catalysts

The effect of temperature variation on the growth of Carbon Nanotubes (CNTs) using Thermal Chemical Vapor Deposition (TCVD) is presented. Nickel and Cobalt (Ni-Co) thin films on Silicon (Si) substrates were used as catalysts in TCVD technique. Acetylene gas was used in CNTs growth process at the controlled temperature ranges from 850-1000 ̊ C. Catalysts and CNTs characterization was carried out ...

متن کامل

Role of growth temperature in CVD synthesis of Carbon nanotubes from Ni-Co bimetallic catalysts

The effect of temperature variation on the growth of Carbon Nanotubes (CNTs) using Thermal Chemical Vapor Deposition (TCVD) is presented. Nickel and Cobalt (Ni-Co) thin films on Silicon (Si) substrates were used as catalysts in TCVD technique. Acetylene gas was used in CNTs growth process at the controlled temperature ranges from 850-1000 ̊ C. Catalysts and CNTs characterization was carried out ...

متن کامل

Evaluation of the Effect of Ni-Co NPs for the Effective Growth of Carbon Nanotubes by TCVD System

A systematic study was conducted to understand the influences of catalyst combination as Ni-Co NPs on carbon nanotubes (CNTs) grown by Chemical Vapor Deposition (TCVD). The DC-sputtering system was used to prepare Co and Ni-Co thin films on silicon substrate. Ni- Co nanoparticles were used as metal catalyst for growing carbon nanotubes from acetylene (C2H2) gas in 850 ̊ C during 15 min. Carb...

متن کامل

Uniform patterned growth of carbon nanotubes without surface carbon

In order to utilize the unique properties of carbon nanotubes in microelectronic devices, it is necessary to develop a technology which enables high yield, uniform, and preferential growth of perfectly aligned nanotubes. We demonstrate such a technology by using plasma-enhanced chemical-vapor deposition ~PECVD! of carbon nanotubes. By patterning the nickel catalyst, we have deposited uniform ar...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2001