Corrosion behavior of nitrogen doped diamond-like carbon thin films in NaCl solutions
نویسندگان
چکیده
Nitrogen doped tetrahedral amorphous carbon (ta-C:N) thin films were grown on p-Si(1 1 1) substrates using filtered cathodic vacuum arc (FCVA) deposition by varying nitrogen flow rate. The effect of nitrogen flow rate on the corrosion performance of the films was investigated through potentiodynamic polarization and immersion tests in 0.6 M NaCl solutions. The polarization results showed that the corrosion resistance of the films dropped with increased nitrogen flow rate due to formation of more sp bonds. The immersion tests revealed that the pH value of the solutions had a significant effect on the corrosion behavior of the ta-C:N films. 2009 Elsevier Ltd. All rights reserved.
منابع مشابه
Investigation of structure, adhesion strength, wear performance and corrosion behavior of platinum/ruthenium/nitrogen doped diamond-like carbon thin films with respect to film thickness
In this study, the corrosion performance of platinum/ruthenium/nitrogen doped diamond-like carbon (PtRuN-DLC) thin films deposited on p-Si substrates using a DCmagnetron sputtering deposition system in a 0.1M NaCl solution was investigated using potentiodynamic polarization test in terms of film thickness. Theeffect of thefilmthickness on the chemical composition, bonding structure, surfacemorp...
متن کاملInvestigation of corrosion behavior of nitrogen doped and platinum/ruthenium doped diamond-like carbon thin films in Hank's solution
متن کامل
Nitrogen-Induced Degradation of Corrosion Resistance of Platinum/Ruthenium/Nitrogen-Doped Diamond-like Carbon Thin Films
An influence of nitrogen incorporation on the chemical composition, bonding structure, surface morphology and activity, adhesion strength, and corrosion resistance of platinum/ruthenium/nitrogen-doped diamond-like carbon PtRuN-DLC thin films deposited on conductive p-Si 100 substrates using dc magnetron sputtering deposition was investigated using X-ray photoelectron spectroscopy, micro-Raman s...
متن کاملEnhancement of adhesion strength and corrosion resistance of nitrogen or platinum/ruthenium/nitrogen doped diamond-like carbon thin films by platinum/ruthenium underlayer
متن کامل
Corrosion behavior of aluminum doped diamond-like carbon thin films in NaCl aqueous solution.
Aluminum doped diamond-like carbon (DLC:Al) thin films were deposited on n-Si(100) substrates by co-sputtering a graphite target under a fixed DC power (650 W) and an aluminum target under varying DC power (10-90 W) at room temperature. The structure, adhesion strength and surface morphology of the DLC:Al films were characterized by X-ray photoelectron spectroscopy (XPS), micro-scratch testing ...
متن کامل