Decay Resistance and Physical Properties of Oil Heat Treated Aspen Wood
نویسنده
چکیده
The decay resistance of oil-heat treated aspen wood (Populus tremula l.) against white rot fungi (Coriolus versicolor) and brown rot fungi (Coniophora puteana) was investigated. Three different temperature stages and two time levels for oil heat treatment for the selection of optimum conditions were determined. Linseed oil as a heating medium was used. The mass loss of treated samples that were exposed to both fungi was significantly lower than that of the control samples. Results also showed improvement in dimensional stability after oil heat treatment. Decay resistance and dimensional stability of aspen wood were increased significantly with temperature increasing, but time seemed to have no effect on those properties. Oil heat treatment is a suitable method to improve decay resistance of aspen wood as it reduced the mass loss by 71% and 77% against Coriolus versicolor and Coniophora puteana compared with control samples, respectively. On the other hand, oil heat treatment improved the dimensional stability by about 20.5%.
منابع مشابه
Densification of Wood Veneers Combined with Oil- Heat Treatment. Part Ii: Hygroscopicity and Mechanical Properties
In an effort to achieve high mechanical performance and improved dimensional stability, densification combined with oil-heat treatment (OHT) was performed. In our previous study, OHT was successfully applied to densified veneer, which resulted in improved dimensional stability. In the present study, the impact of OHT on densified wood veneer hygroscopicity and mechanical properties was determin...
متن کاملEffect of chitosan on the mold resistance of wood and its surface properties
In this study, the effect of soluble chitosan, thyme oil and linseed oil on the mold resistance of wood and its surface properties was investigated. Both low and medium molecular weight chitosan with concentration of 1 and 2% were used. Cypress wood samples with dimensions of 20 × 20 × 70 mm and moisture content of 12% were saturated by the preservatives. The results showed that the maximum abs...
متن کاملUtilization of Temperature Kinetics as a Method to Predict Treatment Intensity and Corresponding Treated Wood Quality: Durability and Mechanical Properties of Thermally Modified Wood
Wood heat treatment is an attractive alternative to improve decay resistance of wood species with low natural durability. However, this improvement of durability is realized at the expense of the mechanical resistance. Decay resistance and mechanical properties are strongly correlated to thermal degradation of wood cells wall components. Mass loss resulting from this degradation is a good indic...
متن کاملThe optimum level of nano-wollastonite consumption as fire-retardant in poplar wood (Populus nigra)
Fire-retarding properties of wollastonite nanofibers in poplar wood (Populus nigra) were studied here. Some physical properties such as water absorption, volumetric swelling and anti-swelling efficiency (ASE) were also measured. Specimens were prepared according to the ISO 11925 specifications for the fire-retarding properties and according to the ASTM D4446 -2002 specifications for th...
متن کاملThe optimum level of nano-wollastonite consumption as fire-retardant in poplar wood (Populus nigra)
Fire-retarding properties of wollastonite nanofibers in poplar wood (Populus nigra) were studied here. Some physical properties such as water absorption, volumetric swelling and anti-swelling efficiency (ASE) were also measured. Specimens were prepared according to the ISO 11925 specifications for the fire-retarding properties and according to the ASTM D4446 -2002 specifications for th...