Effect of Variations in Micropatterns and Surface Modulus on Marine Fouling of Engineering Polymers
نویسندگان
چکیده
We report on the marine fouling and fouling release effects caused by variations of surface mechanical properties and microtopography of engineering polymers. Polymeric materials were covered with hierarchical micromolded topographical patterns inspired by the shell of the marine decapod crab Myomenippe hardwickii. These micropatterned surfaces were deployed in field static immersion tests. PDMS, polyurethane, and PMMA surfaces with higher elastic modulus and hardness were found to accumulate more fouling and exhibited poor fouling release properties. The results indicate interplay between surface mechanical properties and microtopography on antifouling performance.
منابع مشابه
A Review on Crude Oil Fouling and Mitigation Methods in Pre-heat Trains of Iranian Oil Refineries
Crude oil fouling of the equipment surfaces is a troublesome issue which leads to operating difficulties, economic penalties, increased environmental impacts, and health and safety hazards in petroleum industry. With a rough estimation, a minimum cost of equal to 4 million barrels of oil/year is required to be invested to offset the costs of crude oil fouling in Pre-heat Trains of Iranian oil r...
متن کاملInfluence of Temperature and Moisture on the Compressive Strength of Carbon Fiber Reinforced Polymers
The effect of moisture absorption and high temperature on the compressive strength of unidirectional IM7/977-2 carbon/epoxy resins have been investigated experimentally. The specimens were divided into 4 groups, and tested under 4 different conditions by varying the testing temperature and moisture parameters. The fiber orientation selected were 0o, ±45o and 90o...
متن کاملInvestigation of Peak Particle Velocity Variations during Impact Pile Driving Process
Impact pile driving is a multi-component problem which is associated to multi-directional ground vibrations. At first, vibration is transferred from the hammer to the pile and then to the common interface of pile and soil. This is then transferred to the environment and has great impact on the adjacent structures, causing disturbance to residents and also damage to the buildings. It is of high ...
متن کاملPreparation and Characterization of CA−PEG−TiO2 Membranes: Effect of PEG and TiO2 on Morphology, Flux and Fouling Performance
Modified cellulose acetate (CA) membranes were prepared by dissolving the polymers in a mixture of acetone (AC) and N, N dimethylacetamide (DMAc) (70:30) solvent and deionized (DI) water was used in the coagulation bath. The introduction of polyethylene glycol (PEG) additive and TiO2 nanoparticles (NPs) into the casting solution has changed the structures of the resulting membranes during the p...
متن کاملDifference between efficiency of ultrasound treatments above and below the membrane surface in membrane clarification of pomegranate juice
Microfiltration can clarify pomegranate juice; however, fouling is a limiting phenomenon in the process. In current work ultrasound was applied above and below the membrane surface to reduce fouling after removing temperature effect. A hydrophilic mixed cellulose ester membrane with pore size of 0.45 μm was used in lab scale flat sheet module. Membrane module was placed above and below the ultr...
متن کامل