One-pot synthesis of poly (3,4-ethylenedioxythiophene)-Pt nanoparticle composite and its application to electrochemical H2O2 sensor

نویسندگان

  • Li-Chi Chang
  • Huan-Nung Wu
  • Chia-Yu Lin
  • Yi-Hsuan Lai
  • Chih-Wei Hu
  • Kuo-Chuan Ho
چکیده

Poly(3,4-ethylenedioxythiophene)-Pt nanoparticle composite was synthesized in one-pot fashion using a photo-assisted chemical method, and its electrocatalytic properties toward hydrogen peroxide (H2O2) was investigated. Under UV irradiation, the rates of the oxidative polymerization of EDOT monomer along with the reduction of Pt4+ ions were accelerated. In addition, the morphology of PtNPs was also greatly influenced by the UV irradiation; the size of PtNPs was reduced under UV irradiation, which can be attributed to the faster nucleation rate. The immobilized PtNPs showed excellent electrocatalytic activities towards the electroreduction of hydrogen peroxide. The resultant amperometric sensor showed enhanced sensitivity for the detection of H2O2 as compared to that without PtNPs, i.e., only with a layer of PEDOT. Amperometric determination of H2O2 at -0.55 V gave a limit of detection of 1.6 μM (S / N = 3) and a sensitivity of 19.29 mA cm-2 M-1 up to 6 mM, with a response time (steady state, t95) of 30 to 40 s. Energy dispersive X-ray analysis, transmission electron microscopic image, cyclic voltammetry (CV), and scanning electron microscopic images were utilized to characterize the modified electrode. Sensing properties of the modified electrode were studied both by CV and amperometric analysis.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Solid-State Heating Synthesis of Poly (3,4-Ethylenedioxythiophene)/Gold/Graphene Composite and Its Application for Amperometric Determination of Nitrite and Iodate

A ternary composite of poly (3,4-ethylenedioxythiophene)/gold/graphene (PEDOT/Au/GO) for promising electrochemical sensor was synthesized by solid-state heating method. The interaction between the PEDOT, Au, and GO explored for detection of nitrite and iodate. It was found that the PEDOT/Au/GO composite had shale-like morphology with a uniform distribution of gold nanoparticles. Electrochemical...

متن کامل

Morphological Characterization and Analytical Application of Poly(3,4-ethylenedioxythiophene)-prussian Blue Composite Films Electrodeposited in Situ on Platinum Electrode Chips

Electrochemical in situ preparation and morphological characterization of inorganic redox material-organic conducting polymer coatings as thin films on platinum electrodes are presented. Composite inorganic-organic coatings consist of Prussian blue (PB) and [poly(3,4-ethylenedioxythiophene)] (PEDOT), and PEDOT organic polymers doped with ferricyanide (PEDOT-FeCN). The PEDOT coating deposited fr...

متن کامل

Effect of poly(3,4-ethylenedioxythiophene) (PEDOT) in carbon-based composite electrodes for electrochemical supercapacitors

Electrochemical double layer supercapacitor cells were fabricated and tested using composite electrodes of activated carbon with carbon black and poly(3,4-ethylenedioxythiophene) (PEDOT), and an organic electrolyte 1M TEABF4/PC solution. The effect of PEDOT on the performance of the EDLC cells was explored and the cells were characterised by electrochemical impedance spectroscopy (EIS), cyclic ...

متن کامل

Synthesis of Pt-SWCNTS Conductive Nanocomposite by Microwave Heated Polyol Strategy; Application for Amplification of 5-Fluorouracil Anticancer Drug Electrochemical Sensor

In this study, a simple strategy was described for the synthesis of Pt-SWCNTs conductive nanocomposite by microwave heated polyol method and nanocomposite characterized by EDS, FESEM, and XRD method. The Pt nanoparticles were decorated at the surface of SWCNTs with a diameter of 22.3 nm. The synthesized nanocomposite was used for modification of the carbon paste electrode (CPE) in the presence ...

متن کامل

Redox exchange induced MnO2 nanoparticle enrichment in poly(3,4-ethylenedioxythiophene) nanowires for electrochemical energy storage.

MnO2 nanoparticle enriched poly(3,4-ethylenedioxythiophene) (PEDOT) nanowires are fabricated by simply soaking the PEDOT nanowires in potassium permanganate (KMnO4) solution. The structures of these MnO2 nanoparticle enriched PEDOT nanowires are characterized by SEM and TEM, which show that the MnO2 nanoparticles have uniform sizes and are finely dispersed in the PEDOT matrix. The chemical cons...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره 7  شماره 

صفحات  -

تاریخ انتشار 2012