Structural and magneto-transport properties of electrodeposited bismuth nanowires
نویسندگان
چکیده
Arrays of semimetallic Bi nanowires have been successfully fabricated by electrodeposition. Each nanowire consists of elongated Bi grains along the wire direction. Very large positive magnetoresistance of 300% at low temperatures and 70% at room temperature with quasilinear field dependence has been observed. These features are desirable for wide-range field sensing applications. © 1998 American Institute of Physics. @S0003-6951~98!00236-8#
منابع مشابه
Finite-size effects in bismuth nanowires
Arrays of semimetallic Bi nanowires, fabricated by electrodeposition, exhibit strong finite-size effects in transport properties as the carrier mean-free path is limited by the wire dimensions. We have observed a resistivity enhancement, a very large positive magnetoresistance, and a resistance maximum that depends on the strength and orientation of the magnetic field and the nanowire diameter....
متن کاملInvestigations of Microstructures and Magnetic Properties through Off-time between Pulses and Controlled Cu Content in Pulse Electrodeposited NiCu Nanowires
NiCu alloy nanowires arrays were embedded into the anodic aluminum oxide (AAO) template by ac-pulse electrodeposition. Different off-time were used in electrolyte with constant concentration of Ni and Cu and acidity of 3. The effect of deposition parameters on alloy contents was investigated by studying the microstructure and magnetic properties of as-deposited NiCu alloy nanowires. Atomic forc...
متن کاملInvestigations of Magnetic Properties Through Electrodeposition Current and Controlled Cu Content in Pulse Electrodeposited CoFeCu Nanowires
CoFeCu nanowires were deposited by pulsed electrodeposition technique into the porous alumina templates by a two-step mild anodization technique, using the single-bath method. The electrodeposition was performed in a constant electrolyte while Cu constant was controlled by electrodeposition current. The electrodeposition current was 3.5, 4.25, 5 and 6 mA. The effect of electrodeposition current...
متن کاملThermal properties of electrodeposited bismuth telluride nanowires embedded in amorphous alumina
Bismuth telluride nanowires are of interest for thermoelectric applications because of the predicted enhancement in the thermoelectric figure-of-merit in nanowire structures. In this letter, we carried out temperature-dependent thermal diffusivity characterization of a 40 nm diameter Bi2Te3 nanowires/alumina nanocomposite. Measured thermal diffusivity of the composite decreases from 9.2310−7 m2...
متن کاملFaculty of Physics and Astronomy
Thermoelectric Properties of Bismuth Nanowires: Bismuth nanowires were electrochemically deposited in ion track-etched polymer membranes and their transport properties were studied. The Seebeck coefficients of single-and polycrystalline nanowires were measured as a function of wire diameter and temperature. For that purpose, a sample holder was designed that is capable of contacting nanowire ar...