Effect of Electron Beam Irradiation on the Tensile Properties of Oil Palm Mesocarp Fibre/poly(butylene Succinate) Biocomposites

نویسندگان

  • Y. Y. Then
  • N. Zainuddin
  • H. Ariffin
  • Wan Yunus
  • M. F. Abd Rahman
چکیده

The present work deals with the utilization of oil palm mesocarp fibre (OPMF) and poly(butylene succinate) (PBS) to produce cost-effective biodegradable materials. The biocomposite was prepared from OPMF and PBS at a weight ratio of 70:30 via a melt blending technique without addition of any additive. This biocomposite showed relatively low tensile and water resistance properties. As a consequence, it was subjected to electron beam irradiation (EBI) treatment under various irradiation dosages ranging from 5–25 kGy, aiming at improving both its tensile properties and its water resistance. The results indicated that the biocomposite irradiated with 25 kGy of applied dosage showed a considerable improvement of 50% in tensile strength, 780% in tensile modulus and 38% in elongation at break. The water absorption and thickness swelling of the biocomposites were reduced after EBI treatment. The scanning electron microscopy showed improvement of the interfacial adhesion between OPMF and PBS after EBI treatment.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Influence of Fiber Content on Properties of Oil Palm Mesocarp Fiber/Poly(butylene succinate) Biocomposites

Biodegradable and environmentally friendly biocomposites produced by a combination of biodegradable thermoplastics and natural fiber have gained increasing interest in recent years. In this work, eco-friendly biocomposites made from poly(butylene succinate) (PBS) and different weight percentages (10, 30, 50, and 70 wt%) of oil palm mesocarp fiber (OPMF) were fabricated via a melt blending proce...

متن کامل

The Influence of Green Surface Modification of Oil Palm Mesocarp Fiber by Superheated Steam on the Mechanical Properties and Dimensional Stability of Oil Palm Mesocarp Fiber/Poly(butylene succinate) Biocomposite

In this paper, superheated steam (SHS) was used as cost effective and green processing technique to modify oil palm mesocarp fiber (OPMF) for biocomposite applications. The purpose of this modification was to promote the adhesion between fiber and thermoplastic. The modification was carried out in a SHS oven at various temperature (200-230 °C) and time (30-120 min) under normal atmospheric pres...

متن کامل

Enhancement of mechanical and thermal properties of oil palm empty fruit bunch fiber poly(butylene adipate-co-terephtalate) biocomposites by matrix esterification using succinic anhydride.

In this work, the oil palm empty fruit bunch (EFB) fiber was used as a source of lignocellulosic filler to fabricate a novel type of cost effective biodegradable composite, based on the aliphatic aromatic co-polyester poly(butylene adipate-co-terephtalate) PBAT (Ecoflex™), as a fully biodegradable thermoplastic polymer matrix. The aim of this research was to improve the new biocomposites' perfo...

متن کامل

Effect of Fiber Esterification on Fundamental Properties of Oil Palm Empty Fruit Bunch Fiber/Poly(butylene adipate-co-terephthalate) Biocomposites

A new class of biocomposites based on oil palm empty fruit bunch fiber and poly(butylene adipate-co-terephthalate) (PBAT), which is a biodegradable aliphatic aromatic co-polyester, were prepared using melt blending technique. The composites were prepared at various fiber contents of 10, 20, 30, 40 and 50 wt% and characterized. Chemical treatment of oil palm empty fruit bunch (EFB) fiber was suc...

متن کامل

Silane-Treated Basalt Fiber–Reinforced Poly(butylene succinate) Biocomposites: Interfacial Crystallization and Tensile Properties

In this work, an economical modifier silane agent—KH550—was used for surface treatment of basalt fiber. Then, a biodegradable poly(butylene succinate) (PBS)/modified basalt fiber (MBF) biocomposite was successfully developed. The effects of silane treatment and fiber mass content on crystalline structure, isothermal crystallization process and mechanical performance of composites were evaluated...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2014