Superconductivity in the alkali metals
نویسندگان
چکیده
At ambient pressure there are 29 elemental superconductors in the periodic table, none of which is an alkali metal. The first alkali metal to become superconducting under high pressure is Cs followed years later by Li. Alkali metals are believed to be exemplary free-electron systems. The fact that an alkali metal becomes superconducting at all is surprising and is a result of the fact that under pressure it shows marked deviations from free-electron behaviour where, counterintuitively, bands narrow and gaps widen. For this reason the alkali metals are among the most interesting systems known to study in high-pressure experiments and superconductivity is one of their most fascinating properties.
منابع مشابه
Enhancement of Critical Current across Single Grain Boundaries in YBa2Cu3Ox and Search for Superconductivity in Alkali Metals
The ability of single grain boundaries in YBa2Cu3Ox bicrystalline rings to carry electrical current is found to be significantly enhanced under hydrostatic pressure. Nearly hydrostatic pressures are applied to the alkali metals Li, Na, and K. in a search for superconductivity. Whereas Li becomes superconducting above 20 GPa at temperatures as high as 15 K, no superconductivity was observed abov...
متن کاملSuperconductivity above 30 K in alkali-metal-doped hydrocarbon
The recent discovery of superconductivity with a transition temperature (T(c)) at 18 K in K(x)picene has extended the possibility of high-T(c) superconductors in organic materials. Previous experience based on similar hydrocarbons, like alkali-metal doped phenanthrene, suggested that even higher transition temperatures might be achieved in alkali-metals or alkali-earth-metals doped such polycyc...
متن کاملSuperconductivity in room-temperature stable electride and high-pressure phases of alkali metals.
S-band metals such as alkali and alkaline earth metals do not undergo a superconducting transition (SCT) at ambient pressure, but their high-pressure phases do. By contrast, room-temperature stable electride [Ca(24)Al(28)O(64)](4+)⋅4e(-) (C12A7:e(-)) in which anionic electrons in the crystallographic sub-nanometer-size cages have high s-character exhibits SCT at 0.2-0.4 K at ambient pressure. I...
متن کاملIntercalant-independent transition temperature in superconducting black phosphorus
Research on black phosphorus has been experiencing a renaissance over the last years, after the demonstration that few-layer crystals exhibit high carrier mobility and a thickness-dependent bandgap. Black phosphorus is also known to be a superconductor under high pressure exceeding 10 GPa. The superconductivity is due to a structural transformation into another allotrope and accompanied by a se...
متن کاملEnhanced superconducting properties of bicrystalline YBa2Cu3Ox and alkali metals under pressure
Nearly hydrostatic pressures are found to enhance the critical current density Jc through single grain boundaries in YBa2Cu3Ox rings and to induce superconductivity in Li. Whereas Li becomes superconducting above 20 GPa at temperatures as high as 15 K, no superconductivity was observed above 4 K in Na to 65 GPa nor in K above 4 K to 43.5 GPa or above 1.5 K to 35 GPa.