Short-time dynamics of correlated magnetic moments in superparamagnetic Cu–Co melt spun alloys exhibiting giant magnetoresistance
نویسنده
چکیده
منابع مشابه
Magnetic States in Ensemble of Ferromagnetic Nanoparticles in Cu-Mn-Al Alloy
Two Cu-Mn-Al samples of different compositions were studied: one exhibiting martensitic transformation, another without structural transition. X-ray diffraction and magnetic measurements demonstrate that different magnetic behaviors of alloys originate from different concentrations and sizes of ferromagnetic nanoparticles, which appear after solid solution decomposition.Estimation of magnetic m...
متن کاملMagnetic properties and giant magnetoresistance in melt-spun Co-Cu alloys
Magnetic, structural, and transport properties of as-quenched and annealed ColOCugO samples have been investigated using x-ray diffraction and a SQUID magnetometer. The largest value of MR change was observed for the as-quenched sample annealed at 450 “C for 30 min. The magnetic and transport properties closely correlate with the microstructure, mainly with Co magnetic particle size and its dis...
متن کاملAnomaly of Ac Resistance in Magnetic Nanoparticle Alloys at Spin-glass-like Transition
A combined study of magnetic susceptibility and AC resistance was performed on melt-spun Cu-Co granular magnetic ribbons. The AC resistance as a function of temperature has a sharp maximum. We associate it with a diverging correlation length at the temperature of collective freezing of magnetic moments via increasing magnetic losses in the induced non-uniform field. Application of this model to...
متن کاملEffect of Joule-Heating Annealing on Giant Magnetoimpedance of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1 and 2) Melt-Spun Ribbons
In this work, we have studied the influence of dc joule-heating thermal processing on the structure, magnetoimpedance (MI) and thermal properties of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1, and 2) rapidly solidified melt-spun ribbons. The nanocrystallization process was carried out by the current annealing of as-spun samples at various current densities. As-spun and joule-heated samples were studied...
متن کاملساختار و خواص مغناطیسی آلیاژهای CoFeSiB انجماد سریع یافته
The effects of metalloids Si(4-27 at%) and B(5-22 at%) on the structure and magnetic properties of melt spun cobalt based alloys containing 5at% Fe have been studied. XRD results revealed that in non-eutectic ternary CoFeSi and CoFeB alloys, the additions of Si or B, alone can not lead to full amorphization of melt spun ribbons. In quaternary CoFeSiB alloys, the total amounts of Si and B additi...