An experimental study of the influence of autogeneous healing on chloride ingress in cracked concrete is presented. In the study, two concrete mixtures (a Portland cement mix and a blast furnace slag mix), two healing regimes (submerged and fog room regime), two cracking ages (14 and 28 days), and multiple crack widths are used as parameters. An adapted Rapid Chloride Migration testing procedure is used after the healing period to assess the effectiveness of healing. It was found that small bending-type (i.e. tapered) cracks can heal fully, and larger cracks partially under tested conditions. The obtained results provide a good starting point for further study of the influence of autogeneous or self-healing on concrete durability.
منابع مشابه
Quantification of the Service Life Extension and Environmental Benefit of Chloride Exposed Self-Healing Concrete
Formation of cracks impairs the durability of concrete elements. Corrosion inducing substances, such as chlorides, can enter the matrix through these cracks and cause steel reinforcement corrosion and concrete degradation. Self-repair of concrete cracks is an innovative technique which has been studied extensively during the past decade and which may help to increase the sustainability of concr...
متن کاملModeling chloride transport in cracked concrete: a 3-D image–based microstructure simulation
The prediction of the service life of concrete materials is difficult, mainly because of their complex heterogeneous microstructure and their random nature. Studying the presence of cracks in concrete and their effect on chloride transport and binding properties is of great interest in civil engineering. Cracks with different widths and depths will reduce the effective cover thickness and accel...
متن کاملMeasurement and Modeling of the Ability of Crack Fillers to Prevent Chloride Ingress into Mortar.
A common repair procedures applied to damaged concrete is to fill cracks with an organic polymer. This operation is performed to increase the service life of the concrete by removing a preferential pathway for the ingress of water, chlorides, and other deleterious species. To effectively fulfill its mission of preventing chloride ingress, the polymer must not only fully fill the macro-crack, bu...
متن کاملA novel durability design approach for new cementitious materials: Modelling chloride ingress in strain-hardening cement-based composites
To fully utilise the advantageous durability properties of new cementitious materials such as fibre-reinforced Strain-Hardening Cement-based Composites (SHCC), a performance-based durability design approach is required. For crack-free ordinary concrete first promising concepts exist, e.g. the DuraCrete model. However, the parameters of these models, which were quantified for ordinary concrete, ...
متن کاملA comprehensive probabilistic model of chloride ingress in unsaturated concrete
Corrosion induced by chloride ions becomes a critical issue for many reinforced concrete structures. The chloride ingress into concrete has been usually simplified as a di↵usion problem where the chloride concentration throughout concrete is estimated analytically. However, this simplified approach has several limitations. For instance, it does not consider chloride ingress by convection which ...
متن کامل