Effect of preheat repetition on color stability of methacrylate- and silorane-based composite resins
نویسندگان
چکیده
Background. The aim of this study was to investigate the effect of preheating methacrylate- and silorane-based composite resins on their color stability up to 40 times at 55‒60°C. Methods. Seventy-six methacrylate and silorane-based composite resin samples, with a diameter of 10 mm and a height of 2 mm, were divided into 4 groups (n=19). After the samples were prepared, their color parameters were determined using a reflective spectrophotometer. The composite resin samples were separately stored in a solution of tea for 40 consecutive days. Then the samples underwent a color determination procedure again using a spectrophotometer and color changes were recorded. Finally two-way ANOVA was used to study the effect of composite temperature on its staining (P<0.05). Independent-samples t-test was used to evaluate changes in conversion rates of preheated composite resin samples compared to non-heated samples at P=0.005 and P=0.029 for silorane-based and Z250 composite resin samples, respectively. Results. Both composite resin type (P=0.014) and preheating (P<0.001) had significant effects on ΔE. Conclusion. Repeated preheating of methacrylate- and silorane-based composite resin samples, up to 55‒60°C for 40 rounds, resulted in more color changes compared with unheated composite resin samples. After storage in a solution of tea the color change rate in the composite resin samples of silorane-based was higher than the Z250 composite resin samples.
منابع مشابه
Effect of composite shade, curing time and mode on temperature rise of silorane and methacrylate- based composite resins
Introduction: The present study was performed to evaluate the effects of light-curing modes and shades of methacrylate and silorane-based composite resins on temperature rise during polymerization of composite resins. Materials &Methods: In this in vitro study, ninety composite samples with two types of composite resin - methacrylate-based and a low-shrinkage silorane-based were prepared, in...
متن کاملStaining susceptibility of methacrylate and silorane-based materials: influence of resin type and storage time
Introduction: The color stability of composite resins is a fundamental factor in their clinical behavior. Objective: To evaluate the color stability of composite resins of different colors exposed to a colabased soft drink after different storage periods. Additionally, three methacrylate-based materials and one silorane-based material were evaluated. Material and methods: Specimens of three met...
متن کاملInfluence of different staining beverages on color stability, surface roughness and microhardness of silorane and methacrylate-based composite resins.
AIM To investigate the influence of different staining beverages on color stability, surface roughness and microhardness of silorane and methacrylate-based composite resins. MATERIALS AND METHODS Three different composite resins (Filtek Silorane, Filtek P60, Filtek Supreme XT) were tested. Thirty cylindrical specimens (10 × 2 mm) per material were prepared and polished with a series of alumin...
متن کاملEffect of energy drinks on microhardness of silorane and dimethacrylate-based composite resins
Introduction: Increased consumption of energy drinks has raised concerns about their effects on dental restorations. This study assessed the effects of two energy drinks on the surface microhardness of methacrylate and silorane-based composites after 1-week and 1-month periods. Materials & Methods: In this in-vitro study, 90 cubic samples were prepared from Filtek P90, Filtek Z250 and Filtek Z...
متن کاملThe effect of bleaching on microhardness of silorane-based composite resins
Introduction: Bleaching treatments may negatively affect the surface quality of composite restorations existing in the mouth. This study sought to assess the effect of 16% and 35% carbamide peroxide on microhardness of silorane-based versus two methacrylate-based composite resins. Methods: A total of 54 discs were fabricated from FiltekP90 (P90), FiltekZ350XT(Z350) Enamel and Filtek Z250(Z25...
متن کامل