Reactive silver inks for patterning high-conductivity features at mild temperatures.
نویسندگان
چکیده
Reactive silver inks for printing highly conductive features (>10(4) S/cm) at room temperature have been created. These inks are stable, particle-free, and suitable for a wide range of patterning techniques. Upon annealing at 90 °C, the printed electrodes exhibit an electrical conductivity equivalent to that of bulk silver.
منابع مشابه
Preparation of solid silver nanoparticles for inkjet printed flexible electronics with high conductivity.
Silver nanoparticles (NPs) which could be kept in solid form and were easily stored without degeneration or oxidation at room temperature for a long period of time were synthesized by a simple and environmentally friendly wet chemistry method in an aqueous phase. Highly stable dispersions of aqueous silver NP inks, sintered at room temperature, for printing highly conductive tracks (∼8.0 μΩ cm)...
متن کاملTransparent conductive grids via direct writing of silver nanoparticle inks.
Transparent conductive grids are patterned by direct writing of concentrated silver nanoparticle inks. This maskless, etch-free patterning approach is used to produce well-defined, two-dimensional periodic arrays composed of conductive features with center-to-center separation distances of up to 400 µm and an optical transmittance as high as 94.1%.
متن کاملSilver Ink Formulations for Sinter-free Printing of Conductive Films
Inkjet printing offers an attractive method for the deposition of metal interconnects in electronic systems and enables a low-cost, environmentally friendly route to manufacture. However, virtually all current metal inkjet processes require post-deposition sintering treatments to achieve the optimum electrical conductivity, because the growth mechanism involves coalescence of discrete nanoparti...
متن کاملSpray-coated nanoscale conductive patterns based on in situ sintered silver nanoparticle inks
Nanoscale patterns with high conductivity based on silver nanoparticle inks were fabricated using spray coating method. Through optimizing the solution content and spray operation, accurate nanoscale patterns consisting of silver nanoparticles with a square resistance lower than 1 Ω /cm2 were obtained. By incorporating in situ sintering to substitute the general post sintering process, the time...
متن کاملElectrical conductivity anomaly in silver vadadium-tellurite glasses at temperatures higher than a characteristic temperature: evidence for an ionic-nonadiabatic polaronic mixed conduction
Electrical conduction anomaly was observed in the mixed ion-polaron regime for xAg2O-40TeO2-(60-x)V2O5 glassy system with 0 ≤x≤ 50 mol%, which were prepared by common melt quenching method. For the understudied glasses, the temperature dependence of dc electrical conductivity was measured from a characteristic temperature to 380 K, which certified their semiconducting nature. The measured condu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of the American Chemical Society
دوره 134 3 شماره
صفحات -
تاریخ انتشار 2012