Bioinspired design and macroscopic assembly of poly(vinyl alcohol)-coated graphene into kilometers-long fibers.
نویسندگان
چکیده
Nacre is characterized by its excellent mechanical performance due to the well-recognized "brick and mortar" structure. Many efforts have been applied to make nacre-mimicking materials, but it is still a big challenge to realize their continuous production. Here, we prepared sandwich-like building blocks of poly(vinyl alcohol) (PVA)-coated graphene, and achieved high-nanofiller-content kilometers-long fibers by continuous wet-spinning assembly technology. The fibers have a strict "brick and mortar" layered structure, with graphene sheet as rigid brick and PVA as soft mortar. The mortar thickness can be precisely tuned from 2.01 to 3.31 nm by the weight feed ratio of PVA to graphene, as demonstrated by both atomic force microscopy and X-ray diffraction measurements. The mechanical strength of the nacre-mimicking fibers increases with increasing the content of PVA, and it rises gradually from 81 MPa for the fiber with 53.1 wt% PVA to 161 MPa for the fiber with 65.8 wt% PVA. The mechanical performance of our fibers was independent of the molecular weight (MW) of PVA in the wide range of 2-100 kDa, indicating that low MW polymers can also be used to make strong nanocomposites. The tensile stress of fibers immersed in PVA 5 wt% solution reached ca. 200 MPa, surpassing the values of nacre and most of other nacre-mimicking materials. The nacre-mimicking fibers are highly electrically conductive (∼350 S m(-1)) after immersing in hydroiodic acid, enabling them to connect a circuit to illuminate an LED lamp.
منابع مشابه
Crosslinked Electrospun Poly (Vinyl Alcohol) Nanofibers Coated by Antibacterial Copper Nanoparticles
متن کامل
Chitosan/nanosilver Nanofiber Composites with Enhanced Morphology and Microbiological Properties
In recent years natural polymers have been widely used in biomedical applications. Application of natural and biocompatible polymers in wound dressing, medical sutures and tissue engineering are extensively growing. Additional properties are provided when metal nanoparticles such as silver and gold are incorporated in to the fibers. However, nowadays nanofibers due to their inherent properties ...
متن کاملOrdered self-assembly of amphipathic graphene nanosheets into three-dimensional layered architectures.
A novel layered graphene-based architecture is achieved via an ordered self-assembly process. Amphipathic graphene nanosheets are joined horizontally into large sheets via edge splicing, and a cross-linking agent of poly(vinyl alcohol) bridges them into integrated three-dimensional monoliths with tunable interlayer spacing. This layered architecture possesses highly ordered and favorable microc...
متن کاملSynergistic toughening of bioinspired poly(vinyl alcohol)-clay-nanofibrillar cellulose artificial nacre.
Inspired by the layered aragonite platelet/nanofibrillar chitin/protein ternary structure and integration of extraordinary strength and toughness of natural nacre, artificial nacre based on clay platelet/nanofibrillar cellulose/poly(vinyl alcohol) is constructed through an evaporation-induced self-assembly technique. The synergistic toughening effect from clay platelets and nanofibrillar cellul...
متن کاملBioinspired green composite lotus fibers.
Owing to the growing global environmental problems, demands for environmentally friendly, fully biodegradable sustainable composites have substantially increased across various industries. Inspired by the composite structure of cocoon silk, we fabricated a fully green composite fiber (GCF) that is based on the lotus fiber (LF) and a biodegradable polymer, namely poly(vinyl alcohol) (PVA). After...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- Nanoscale
دوره 5 10 شماره
صفحات -
تاریخ انتشار 2013