ZnO nanoparticles embedded in sapphire fabricated by ion implantation and annealing.
نویسندگان
چکیده
ZnO nanoparticles were fabricated in sapphire (α-Al(2)O(3) single crystal) by Zn ion implantation (48 keV) at an ion fluence of 1 × 10(17) cm(-2) and subsequent thermal annealing in a flowing oxygen atmosphere. Transmission electron microscopy (TEM) analysis revealed that metallic Zn nanoparticles of 3-10 nm in dimensions formed in the as-implanted sample and that ZnO nanoparticles of 10-12 nm in dimensions formed after annealing at 600 °C. A broad absorption band, peaked at 280 nm, appeared in the as-implanted crystal, due to surface plasma resonance (SPR) absorption of metallic Zn nanoparticles. After annealing at 600 °C, ZnO nanoparticles resulted in an exciton absorption peak at 360 nm. The photoluminescence (PL) of the as-implanted sample was very weak when using a He-Cd 325 nm line as the excitation source. However, two emission peaks appeared in the PL spectrum of ZnO nanopraticles, i.e., one ultraviolet (UV) peak at 370 nm and the other a green peak at 500 nm. The emission at 500 nm is stronger and has potential applications in green/blue light-emitting devices.
منابع مشابه
Photoluminescence of SnO2 nanoparticles embedded in Al2O3
Tetragonal Sn nanoparticles of ∼15 nm diameter are produced in Al2O3 by direct Sn implantation at room temperature. After thermal annealing at 1000 ◦C in oxygen, the implantation-induced amorphous region recrystallized and the Sn nanoparticles turned into SnO2 nanoparticles with an average diameter of ∼30 nm as revealed by transmission electron microscopy. While no absorption and photoluminesce...
متن کاملPhotocatalytic Activity and Stability of Porous Polycrystalline ZnO Thin-Films Grown via a Two-Step Thermal Oxidation Process
The photocatalytic activity and stability of thin, polycrystalline ZnO films was studied. The oxidative degradation of organic compounds at the ZnO surface results from the ultraviolet (UV) photo-induced creation of highly oxidizing holes and reducing electrons, which combine with surface water to form hydroxyl radicals and reactive oxygen species. Therefore, the efficiency of the electron-hole...
متن کاملDesignable buried waveguides in sapphire by proton implantation
Buried and stacked planar as well as buried single and parallel channel waveguides are fabricated in sapphire by proton implantation. Good control of the implantation parameters provides excellent confinement of the guided light in each structure. Low propagation losses are obtained in fundamental-mode, buried channel waveguides without postimplantation annealing. Choice of the implantation par...
متن کاملHigh Mobility SiGe/Si Transistor Structures on Sapphire Substrates Using Ion Implantation
High mobility n-type SiGe/Si transistor structures have been fabricated on sapphire substrates by ion implanting phosphorus ions into strained 100 for the first time. The strained Si channels were sandwiched between Sio.7Geo.3 layers, which, in turn, were deposited on Sio.7Geo.3 virtual substrates and graded SiGe buffer layers. After the molecular beam epitaxy (MBE) film growth process was comp...
متن کاملEffect of Laser Annealing on Optical Properties of Ion-Implanted ZnO Nanorods
We report on the demonstration of the effectiveness of nanosecond laser annealing on optical properties of phosphorus ion (P)-implanted ZnO nanorods (NRs). Vertically-alligned ZnO NRs have been synthesized by nanoparticle-assisted pulsed laser deposition (NAPLD) on c-plane sapphire substrates. The pre-laser annealing was performed with the third harmonic (355 nm) of a Qwitched Nd:YAG laser at a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Nanotechnology
دوره 17 10 شماره
صفحات -
تاریخ انتشار 2006