Calorimetry of hydrogen desorption from a-Si nanoparticles
نویسندگان
چکیده
J. Farjas, D. Das, J. Fort, P. Roura, and E. Bertran GRMT, Departament de Fı́sica, Universitat de Girona, Campus Montilivi, Edif.PII, E17071-Girona, Catalonia, Spain Department of Physics, Ramakrishna Mission College, Narendrapur IY3508, West Bengal, India FEMAN, Departament de Fı́sica Aplicada i Optica, Universitat de Barcelona, Diagonal 647, 4 planta, E08028-Barcelona, Catalonia, Spain ~Received 11 July 2001; revised manuscript received 3 October 2001; published 15 February 2002!
منابع مشابه
Thermally induced structural transformations on polymorphous silicon
Polymorphous Si is a nanostructured form of hydrogenated amorphous Si that contains a small fraction of Si nanocrystals or clusters. Its thermally induced transformations such as relaxation, dehydrogenation, and crystallization have been studied by calorimetry and evolved gas analysis as a complementary technique. The observed behavior has been compared to that of conventional hydrogenated amor...
متن کاملEnhancement of oxidation rate of a-Si nanoparticles during dehydrogenation
Oxidation of amorphous silicon (a-Si) nanoparticles grown by plasma-enhanced chemical vapor deposition were investigated. Their hydrogen content has a great influence on the oxidation rate at low temperature. When the mass gain is recorded during a heating ramp in dry air, an oxidation process at low temperature is identified with an onset around 250 °C. This temperature onset is similar to tha...
متن کاملEco-Friendly Synthesis and Characterization of Ni-Si Nanoparticles Mixed Oxides as Catalyst for
The nanoparticles of Ni–Si mixed oxides were prepared by co-precipitation method using nickel nitrate; Ni(NO3)2 6H2O and tetraethylorthosilicate (TEOS). The products were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), and hydrogen temperature program reduction (H2-TPR). The results revealed that Ni–Si mixed oxides particles were obtained with average particle ...
متن کاملCharacteristics of the absorption and the emission of hydrogen in palladium nanoparticles encapsulated into graphite at 1.0 MPa hydrogen pressure
Palladium nanoparticles encapsulated into graphite (Pd–graphite intercalation compound: Pd–GIC) were produced from two kinds of graphite, natural graphite (average flake size: 270 mm) and kish graphite (average flake size: 15 mm). Hydrogen storage properties of Pd– GIC have been investigated by means of differential scanning calorimetry (DSC) between 473 and 573 K at 1.0 MPa hydrogen pressure. ...
متن کاملEffect of Milling Time on Hydrogen Desorption Properties of Nanocrystalline MgH2
Nanocrystalline magnesium hydride powder was synthesized by mechanical milling of MgH2 in a planetary ball mill for various times. The effect of MgH2 structure, i.e. crystallite size, lattice strain, particle size and specific surface area on the hydrogen desorption properties was investigated. A single peak of hydrogen desorption was observed for as-received powder, exhibiting an average parti...