Low Temperature Thermochemical Treatments of Austenitic Stainless Steel Without Impairing Its Corrosion Resistance
نویسندگان
چکیده
منابع مشابه
The Evaluation of Corrosion Behavior of AISI 347 Stainless Steel to ASTM A335 Low Alloy Steel Dissimilar Welds
In the present study, the corrosion behavior of AISI 347 austenitic stainless steel to ASTM A335 low alloy steel dissimilar joint was investigated. For this purpose, two filler metals, ER309L and ERNiCr-3, were selected to be used during the gas tungsten arc welding process. To investigate the corrosion behavior of the joints after welding, the specimens were tested in 3.5% sodium chloride solu...
متن کاملStainless Steel Type 316Ti
Allegheny Ludlum Type 316Ti (UNS S31635) is a titanium stabilized version of Type 316 molybdenum-bearing austenitic stainless steel. It is also known as DIN/EN designation No. 1.4571. The Type 316 alloys are more resistant to general corrosion and pitting/crevice corrosion than the conventional chromium-nickel austenitic stainless steels such as Type 304. They also offer higher creep, stress-ru...
متن کاملThe Inhibition Effect of Polyethylenimine (PEI) on Pitting Corrosion of 304 Austenitic Stainless Steel in 3.5% NaCl Solution
One of the problems in the case of stainless steels is their low corrosion resistance against pitting corrosion in chloride containing environments, thereby leading to severe damage to industries. In this research, the pitting corrosion of 304 austenitic stainless steel was studied in 3.5% NaCl solution at room temperature (25˚C) by performing electrochemical measurements (containing cyclic pol...
متن کاملOn the Improvement of the Fatigue Behaviour of Austenitic Stainless Steels Due to Surface Residual Stresses Produced by Low Temperature Carburizing
Low temperature carburizing (LTC) treatment improves surface hardness and wear resistance of the austenitic stainless steels without reducing their corrosion resistance. Surface hardness over 1000 Vickers and compressive residual stresses whose modulus exceeds 1500 MPa are usually achieved in the carburized layer, thanks to the formation of the so-called “S-phase”, a carbonsupersaturated austen...
متن کاملCytotoxicity study of plasma-sprayed hydroxyapatite coating on high nitrogen austenitic stainless steels.
Stainless steel has been frequently used for temporary implants but its use as permanent implants is restricted due to its low pitting corrosion resistance. Nitrogen additions to these steels improve both mechanical properties and corrosion resistance, particularly the pitting and crevice corrosion resistance. Many reports concerning allergic reactions caused by nickel led to the development of...