Vertical charge transport in conjugated polymers

Conjugated polymers are novel organic electronic materials highly important for organic photovoltaic applications. Charge transport is one of the key properties which defines the performance of conjugated polymers in electronic devices. This work aims to explore the charge transport anisotropy in thin films of P3HT, one of the most common conjugated polymers. Using X-ray diffraction techniques and charge transport measurements, the relation between vertical charge transport through thin P3HT films and structure of the films was established. It was shown that particular orientations of crystalline domains of P3HT, namely face-on and chain-on, are beneficial for vertical charge transport. These orientations provide the efficient pathways for the charges to be transported vertically, either via π-π stacking interaction between the adjacent conjugated chains, or via the conjugated chain backbones. It was also demonstrated that particular orientations of crystallites are favourable for the formation of interconnected percolated pathways providing enhanced vertical charge transport across the film. Deposition of P3HT on most commonly used silicon substrates typically results in the formation of mostly edge-on orientation of crystallites which is unfavourable for vertical charge transport. Nanoimprint lithography was demonstrated as a powerful processing method for reorienting the edge-on crystalline domains of P3HT into chain-on (vertical) orientation. It is also shown that thin P3HT films with preferentially face-on orientations of crystallites can be deposited on graphene surface by spin coating. Using patterning of thin P3HT films by nanoimprint lithography, unprecedentedly high average vertical mobilities in the range of 3.1-10.6 cm V s were achieved in undoped P3HT. These results demonstrate that charge transport in thin films of a relatively simple and well-known conjugated polymer P3HT can be significantly improved using optimisation of crystallinity, orientation of crystallites, polymer chain orientation and alignment in the films.