Stable p- and n-type doping of few-layer graphene/graphite

ZnMg and NbCl5 were intercalated in graphite and the presence of such molecules between the graphene sheets results in nand p-type doping, respectively. The doping effect is confirmed by Hall and Raman measurements and the intercalation process is monitored by scanning tunneling microscopy. After intercalation the carrier concentration increase almost an order of magnitude and reaches values as high as 10and 10 cm 3 for pand n-type doping, respectively. For higher intercalation times, the intercalated graphite turns back to be as ordered as pristine one as evidenced by the reduction in the D peak in Raman measurements. Intercalation compounds show remarkable stability allowing us to permanently tune the physical properties of few-layer graphite. Our study has provided a new route to produce stable and functional graphite intercalation compounds and the results can be applied to other graphitic structures such as few-layer graphene