Ultrasound-Assisted Pd Activation Process for Electroless Silver Plating
نویسندگان
چکیده
An ultrasound-assisted activation method for electroless silver plating is presented in this study. When the ultrasound was applied during the activation step, the amount of the Pd species adsorbed on substrate surfaces was higher than that of sample pretreated with a conventional activation process without ultrasound irradiation. With this activation method, it was also shown that the adsorbed Pd species with a size of about 5 nm were uniformly distributed on the surfaces, thus a smooth and uniform coating on the surfaces was obtained by subsequent electroless silver plating. The samples after each step were characterized by AFM, XPS, FIB, and SEM. Keywords—Cavitation, Electroless silver, Pd activation, Ultrasonic
منابع مشابه
Preparation of Pd composite membrane via organic-inorganic activation method in electroless plating technique
A palladium composite membrane was prepared via electroless plating technique using organic-inorganic method during activation process. The ceramic support surface was modified by two TiO2-boehmite and one γ-alumina layers to avoid Pd penetration in support pores. Thin and defect-free Pd composite membrane was obtained by creating a relative smoothness on the ceramic support and using Pd nanopa...
متن کاملNovel Electroless Plating of Ruthenium for Fabrication of Palladium-Ruthenium Composite Membrane on PSS Substrate and Its Characterization
This paper focused on a novel method of electroless plating ruthenium (Ru) on solid or porous substrates like porous stainless steel (PSS) discs or ceramic tubes. A novel complexing plating bath of Ru was developed. It is proven that Ru can be deposited directly on these substrates by the bath at a temperature of 328 K and strong alkaline environment. TGA, SEM, EDX and XRD confirmed the success...
متن کاملDeveloping of Ethylene Glycol as a New Reducing Agent for Preparation of Pd-Ag/PSS Composite Membrane for Hydrogen Separation
In the present work, for the first time, a palladium-silver membrane has been prepared by electroless plating on the surface of a porous stainless steel disk by using ethylene glycol as a new reducing agent and polyol process. The reducing action of ethylene-glycol in the presence of PVP as a protecting surface agent produces a membrane with finely divided powder and nano-sized pores. Furthermo...
متن کاملFormation of silicon nanowire packed films from metallurgical-grade silicon powder using a two-step metal-assisted chemical etching method
In this work, we use a two-step metal-assisted chemical etching method to produce films of silicon nanowires shaped in micrograins from metallurgical-grade polycrystalline silicon powder. The first step is an electroless plating process where the powder was dipped for few minutes in an aqueous solution of silver nitrite and hydrofluoric acid to permit Ag plating of the Si micrograins. During th...
متن کامل