Combinatorial Pulsed Laser Deposition of Ag-containing Calcium Phosphate Coatings
نویسندگان
چکیده
G. SOCOL, M. SOCOL, L. SIMA, S. PETRESCU, M. ENCULESCU, F. SIMA, M. MIROIU, G. POPESCU-PELIN, N. STEFAN, R. CRISTESCU, C.N. MIHAILESCU, A. STANCULESCU, C. SUTAN, I.N. MIHAILESCU National Institute for Lasers, Plasma and Radiation Physics, Magurele, Ilfov, Romania National Institute of Materials Physics, Magurele, Ilfov, Romania Institute of Biochemistry, Splaiul Independentei 296, Bucharest, Romania University of Pitesti, Research Centre for Advanced Materials, Targul din Vale Street, No 1, 110040, Pitesti, Arges, Romania
منابع مشابه
Hydroxyapatite coatings grown by pulsed laser deposition with a beam of 355 nm wavelength
Calcium phosphate coatings, obtained at different deposition rates by pulsed laser deposition with a Nd:YAG laser beam of 355 nm wavelength, were studied. The deposition rate was changed from 0.043 to 1.16 Å/shot by modification of only the ablated area, maintaining the local fluence constant to perform the ablation process in similar local conditions. Characterization of the coatings was perfo...
متن کاملPulsed Laser Deposition of SiO
Thin films of bioactive glass-ceramic have been deposited on titanium substrates by the Pulsed Laser Deposition (PLD) technique under different experimental conditions. The effect of parameters such as deposition pressure and temperature of heat treatments was studied. The microstructure and the crystalline phases of the coatings were characterized using SEM, EDX and XRD analysis; the phases pr...
متن کاملEffect of pulsed current densities on co-electrodeposition of Graphene Oxide/ Calcium-Phosphate coatings and their biocompatibility
In this study, calcium-phosphate (Ca-P) and graphene oxide (GO)/ calcium-phosphate (Ca-P) coatings were electrodeposited with different pulsed current densities on TiO2 nanotubes. Results showed that the co-electrodeposition rate in the presence of GO, especially at low current densities of 2 and 5 mA/cm2, significantly decreased. This might be due to the large size of GO sheets as compared to ...
متن کاملCalcium Phosphate Bioceramics with Tailored Crystallographic Texture for Controlling Cell Adhesion
The orientation distribution of crystalline grains in calcium phosphate coatings produced by pulsed laser deposition was investigated using an X-ray pole-figure diffractometer. Increased laser energy density of a KrF excimer laser in the 4–7 J/cm range leads to the formation of hydroxyapatite grains with the c-axis preferentially aligned perpendicularly to the substrates. This preferred orienta...
متن کاملNano-Ag-loaded hydroxyapatite coatings on titanium surfaces by electrochemical deposition.
Hydroxyapatite (HA) coatings on titanium (Ti) substrates have attracted much attention owing to the combination of good mechanical properties of Ti and superior biocompatibility of HA. Incorporating silver (Ag) into HA coatings is an effective method to impart the coatings with antibacterial properties. However, the uniform distribution of Ag is still a challenge and Ag particles in the coating...
متن کامل