Spark-plasma-sintering (SPS) of nanostructured titanium carbonitride powders

Spark-Plasma-Sintering (SPS) compaction experiments of nanostructured titanium carbonitride powders have been performed at 1600°C and 1800°C (sintering time = 1 min). The as-received nanostructured samples have been synthesized by rapid condensation from the gas-phase (high frequency plasma). The sintering results were compared with data obtained by various conventional sintering techniques such as pressureless sintering, gas pressure sintering, and hot pressing. The phase composition and the crystallite size were investigated by X-ray diffraction (XRD). The fracture surfaces of the sintered samples were inspected by scanning electron microscopy (SEM). The experiments show that the SPS method is capable to obtain high densities (~94% of theoretical density) combined with lower grain-size quotient d/d0 of 5.4 6.5.