Numerical Simulation of the Early Age Three-Dimensional Microstructure Development of Cement Pastes
نویسندگان
چکیده
The formation process of microstructure in cement pastes was first simulated with a numerical model CEMHYD3D. The influence of water-to-cement ratio and particles size on heat release and degree of hydration were then investigated. In addition, the mass of CH and C–S–H phases simulated have been verified by measuring values by thermogravimetry–differential scanning calorimetry (TG-DSC) and X-ray diffraction (XRD)-Rietveld analysis. The evolutions of solids phase percolation and capillary pores de-percolation were also identified by means of a three-dimensional (3D) numerical model. The results show that the simulated values are in good agreement with the available experimental data, indicating a good reliability of the CEMHYD3D model.
منابع مشابه
Early Age Properties of Portland Cement Pastes Investigated with Ultrasonic Shear Waves and Numerical Simulation
In this paper, the correlation of reflection loss measured by an ultrasonic shear wave reflection method and the microstructure in cement-based material is investigated. Three cement pastes (Portland cement type I) with different water-cement ratios (0.35, 0.50 and 0.60) cured at 25 °C were examined. The ultrasonic shear wave reflection factor (WRF) was measured by the wave reflection technique...
متن کاملThe Effect of Curing Temperature on the Properties of Cement Pastes Modified with TiO2 Nanoparticles
This paper investigates the effect of curing temperature on the hydration, microstructure, compressive strength, and transport of cement pastes modified with TiO₂ nanoparticles. These characteristics of cement pastes were studied using non-evaporable water content measurement, X-ray diffraction (XRD), compressive strength test, electrical resistivity and porosity measurements, and scanning elec...
متن کاملCompressive strength of Portland cement pastes and mortars containing Cu-Zn nano-ferrite
This study is concerned with the synthesizing of Cu-Zn nano-ferrite particles in the laboratory applying simple techniques. The morphology of the synthesized nano-particles was analyzed using Transmission Electron Microscopy (TEM), and the minerals were identified using X-ray diffraction (XRD). The nano material was used to replace 1- 4 percent by weight of Portland cement in cement pastes and ...
متن کاملInfluence of Cement Particle-Size Distribution on Early Age Autogenous Strains and Stresses in Cement-Based Materials
The influence of cement particle-size distribution on autogenous strains and stresses in cement pastes of identical waterto-cement ratios is examined for cement powders of four different finenesses. Experimental measurements include chemical shrinkage, to quantify degree of hydration; internal relative humidity development; autogenous deformation; and eigenstress development, using a novel embe...
متن کاملCompressive strength of Portland cement pastes and mortars containing Cu-Zn nano-ferrite
This study is concerned with the synthesizing of Cu-Zn nano-ferrite particles in the laboratory applying simple techniques. The morphology of the synthesized nano-particles was analyzed using Transmission Electron Microscopy (TEM), and the minerals were identified using X-ray diffraction (XRD). The nano material was used to replace 1- 4 percent by weight of Portland cement in cement pastes and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2014