Low shrinkage composite resins: influence on sealing ability in unfavorable C-factor cavities.

نویسندگان

  • Eliza Burlamaqui Klautau
  • Karina Kato Carneiro
  • Marcelo Figueiredo Lobato
  • Sissy Maria Mendes Machado
  • Mário Honorato Silva e Souza
چکیده

The present investigation observed the sealing ability of low shrinkage composite resins in large and deep cavities, placed and photocured in one increment. Large, deep cavities (5.0 mm diameter and 2.5 mm deep) surrounded by enamel were prepared in bovine teeth, which were then divided into five groups. Groups 1, 2, 3 and 4: acid conditioning + Adper Single Bond (3M/ESPE, St Paul, MN, USA) and restoration with Aelite LS Posterior (BISCO Inc. Schaumburg, IL, USA) (G1); Filtek Z-350 (3M/ESPE,St Paul, MN, USA) (G2); Filtek Z-350 Flow (3M/ESPE, St Paul, MN, USA) (G3); Premisa (KERR Corporation, Orange, CA, USA) (G4). Group 5: Silorane Adhesive system (3M/ESPE, St Paul, MN, USA) + restoration with Filtek Low Shrinkage Posterior P90 (3M/ESPE, St Paul, MN, USA). After polymerization, the teeth were immersed in 0.5% basic fuchsine solution and immediately washed. Using the Imagetool Software, the extent of dye along the margins was calculated as a percentage of total perimeter. The restorations were then transversally sectioned and the depth of dye penetration was calculated in mm, using the same software. Kruskal-Wallis analysis for all groups showed no statistical differences for extent (p = 0.54) or depth (p = 0.8364) of dye penetration. According to this methodology, the so-called low shrinkage composite resins had the same sealing ability compared to regular and flowable nanocomposite materials.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Marginal Microleakage of Low-shrinkage Composite Silorane in Primary Teeth: An In Vitro Study

BACKGROUND AND AIMS Despite the increasing demand for adhesive restorations in pediatric dentistry, polymerization shrinkage and subsequent marginal microleakage remains a problem. The aim of this study was to evaluate of the sealing ability of novel low-shrinkage composite silorane in class V cavity of primary canines in comparison with three types of composite resin. MATERIALS AND METHODS N...

متن کامل

Microleakage assessment of one- and two-step self-etch adhesive systems with ‎the low shrinkage composites

BACKGROUND AND AIM: Different studies evaluating one-step self-etch (SE) adhesive systems show contradictory findings, so the aim of this study was to compare the microleakage of one-step SE adhesive systems and CLEARFIL SE BOND (that serves as the “gold-standard” SE adhesive) with low shrinkage composites. METHODS: In this in vitro study, Class V cavities with the occlusal margin in enamel and...

متن کامل

مقایسه‌ی میزان ریزنشت حفرات کلاس II ترمیم شده با کامپوزیت‌های سایلوران و متاکریلات بیس با استفاده از دوروش مختلف ترمیمی (روش ساندویچ باز، باندینگ)

Background and Objective: Polymerization shrinkage in composite resins is responsible for microleakage restoration. A recently introduced composite resin Filtek P90 is based on siloxanes and oxiranes which polymerize by cationic "ring opening" polymerization resulting in reduced polymerization shrinkage. The aim of this study was comparative evaluation of microleakage in class II cavities resto...

متن کامل

اثر جهت نوردهی بر ریزنشت دو نوع کامپازیت مایکروفیلد و هایبرید

Introduction: One of the most important factors affecting the marginal seal of composite restorations is polymerization shrinkage. The aim of this study was to evaluate the micro leakage of two resin composites cured with two light directions. Methods: In this experimental study, forty similar class III preparations were prepared in 40 human anterior teeth. The teeth were randomly divided in t...

متن کامل

اثر سه روش مختلف ترمیم بر میزان ریزنشت جینجیوالی کامپوزیت با پایه سایلوران در ترمیم های کلاس II

Background and purpose: Microleakage occurs in posterior composite restorations due to polymerization shrinkage. In recent years low shrinkage silorane-based composites have been introduced to reduce microleakage. The aim of this study was to evaluate the effect of three different restoration techniques on gingival microleakage of a silorane-based composite in class II restorations. Materials ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Brazilian oral research

دوره 25 1  شماره 

صفحات  -

تاریخ انتشار 2011