Thin films of NiO were fabricated in air by surface-oxidation epitaxy (SOE) on biaxially-textured Ni substrate, for use as buffer layers for YBCO coated conductors. The surface-oxidation conditions such as the temperature and the reaction time, as well as the cooling rate, playa determining role in the process of epitaxial growth of the NiO layer. A continuous, biaxially-aligned textured NiO layer, was obtained for a 10 min oxidation in air at 1120°C,and acooling rate of 150 Klh. The roughness of the NiO layer is mostly controlled by a coarsening of some NiO grains .
منابع مشابه
EPITAXIAL YBa 2 Cu 307 ON BIAXIALLY TEXTURED ( 001 ) NI : AN APPROACH TO HIGH CRITICAL CURRENT DENSITY SUPERCONDUCTING TAPES
In-plane aligned, c-axis oriented YBazCu307 (YBCO) films with superconducting critical current densities, Jc, as high as 700,000 amperes per square centimeter at 77 kelvin have been grown on thermo-mechanically, rolled-textured (00 1) Ni tapes using pulsed-laser deposition. Epitaxial growth of oxide buffer layers directly on biaxially textured Ni, formed by recrystallization of cold-rolled pure...
متن کاملDevelopment of cube textured Ni-W alloy substrates used for coated conductors
It is considered as a challenge for RABiTS route to get cube textured Ni-W alloy substrates with high mechanical and magnetic properties for coated conductors. The works of our group in recent years are summarized about different Ni-W substrates with high W content and composite tapes made by RABiTS technique. The fabrication process and the mechanism of cube texture formation in above differen...
متن کاملChemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes
CeO2/La2Zr2O7 composite buffer layers were deposited on Ni-W tapes using chemical solution method. YBa2Cu3O7-x (YBCO) films were then deposited on the CeO2/La2Zr2O7 composite buffer layers using a low-fluorine solution route. Effect of the annealing temperature and annealing atmosphere on the texture of the CeO2 layers was investigated. It was found that CeO2 film annealed at 1000°C under the a...
متن کاملThe manufacturing of an electroplated Ni layer on textured Cu substrate for Cu-based HTS coated conductors
Abstract A sharp cube textured Ni overlayer on Cu substrates has been developed for the manufacturing of long-length RABiTS-based coated conductor tapes. Using a low-cost, non-vacuum and easily scalable technique of electroplating, smooth, crack-free and continuous Ni overlayers were deposited on cube textured Cu substrates without any intermediate layers. In addition, sharp cube textured Sm-do...
متن کاملFerroelectric BaTiO3 thin films on Ni metal tapes using NiO as buffer layer
Ferroelectric BaTiO3 BTO thin films were deposited on NiO buffered polycrystalline Ni tapes by pulsed laser deposition. Microstructural studies by x-ray diffractometer and transmission electron microscopy reveal that the as-grown BTO films have the nanopillar structures with an average size of approximately 80 nm in diameter and the good interface structures with no interdiffusion or reaction. ...
متن کامل