Carbonisation of Resorcinol-Formaldehyde Organic Xerogels: Effect of Temperature, Particle Size and Heating Rate on the Porosity of Carbon Xerogels

Resorcinol-Formaldehyde organic xerogels with an initial pH of 6.5 were synthesized in a microwave oven and then carbonised in a furnace. The influence of the carbonisation temperature, heating rate and the particle size of the organic xerogels upon the pore structure of the carbon xerogels was assessed. The textural properties of the organic and carbon xerogels were evaluated from N2 adsorption-desorption isotherms at -196oC and by measuring the true (helium) density. As the carbonisation temperature increased from 700 to 950oC the SBET of the carbon xerogels decreased from 585 to 471 m 2 g -1 for the carbon xerogels derived from the organic xerogels crushed to a particle size > 212 μm. A decrease in the particle size to dp < 212 μm caused an increase in the BET specific surface area of the carbon xerogels of between 12 and 27% but also a decrease of the carbon xerogel yield of between 15 and 24%, depending on the carbonisation temperature. The pore structure of the carbon xerogels did not change significantly with the increase in the heating rate in the carbonisation process over the interval studied.