High Mobility Thin Film Transistors Based on Amorphous Indium Zinc Tin Oxide
نویسندگان
چکیده
Top-contact bottom-gate thin film transistors (TFTs) with zinc-rich indium zinc tin oxide (IZTO) active layer were prepared at room temperature by radio frequency magnetron sputtering. Sintered ceramic target was prepared and used for deposition from oxide powder mixture having the molar ratio of In2O3:ZnO:SnO2 = 2:5:1. Annealing treatment was carried out for as-deposited films at various temperatures to investigate its effect on TFT performances. It was found that annealing treatment at 350 °C for 30 min in air atmosphere yielded the best result, with the high field effect mobility value of 34 cm2/Vs and the minimum subthreshold swing value of 0.12 V/dec. All IZTO thin films were amorphous, even after annealing treatment of up to 350 °C.
منابع مشابه
Effect of direct current sputtering power on the behavior of amorphous indium-gallium- zinc-oxide thin-film transistors under negative bias illumination stress: A combination of experimental analyses and device simulation
Articles you may be interested in Asymmetrical degradation behaviors in amorphous InGaZnO thin-film transistors under various gate and drain bias stresses Investigation on the negative bias illumination stress-induced instability of amorphous indium-tin-zinc-oxide thin film transistors Appl. Temperature dependence of negative bias under illumination stress and recovery in amorphous indium galli...
متن کاملInvestigation on the negative bias illumination stress-induced instability of amorphous indium-tin-zinc-oxide thin film transistors
Articles you may be interested in A thermalization energy analysis of the threshold voltage shift in amorphous indium gallium zinc oxide thin film transistors under simultaneous negative gate bias and illumination Instability of amorphous hafnium-indium-zinc-oxide thin film transistors under negative-bias-illumination stress Appl. Investigation of zinc interstitial ions as the origin of anomalo...
متن کاملHigh performance InGaZnO thin film transistor with InGaZnO source and drain electrodes
Articles you may be interested in Mobility enhancement in amorphous InGaZnO thin-film transistors by Ar plasma treatment Appl. Correlation of photoconductivity response of amorphous In–Ga–Zn–O films with transistor performance using microwave photoconductivity decay method Appl. Fully transparent InGaZnO thin film transistors using indium tin oxide/graphene multilayer as source/drain electrodes...
متن کاملHydrogen Bistability as the Origin of Photo-Bias-Thermal Instabilities in Amorphous Oxide Semiconductors
The lack of transparency and high temperature processing in silicon-based electronics prevent their applications in transparent Zinc-based metal oxide semiconductors have attracted attention as an alternative to current silicon-based semiconductors for applications in transparent and fl exible electronics. Despite this, metal oxide transistors require signifi cant improvements in performance an...
متن کاملCompositional influence on the electrical performance of zinc indium tin oxide transparent thin-film transistors
In this work, zinc indium tin oxide layers with different compositions are used as the active layer of thin film transistors. This multicomponent transparent conductive oxide is gaining great interest due to its reduced content of the scarce indium element. Experimental data indicate that the incorporation of zinc promotes the creation of oxygen vacancies. In thin-film transistors this effect l...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 10 شماره
صفحات -
تاریخ انتشار 2017