Hot Corrosion Behavior of Sputtered Nanocrystalline Coating with Yttrium Addition at 900 °C
نویسندگان
چکیده
The high temperature corrosion behavior of sputtered nanocrystalline K38 coating with and without yttrium addition under mixed molten salt film in air was investigated. Accelerated corrosion occurred on the coating without yttrium (Y) addition locally after 60 h exposure at 900 °C, which resulted in negative weight gain in kinetics. A uniform and protective alumina scale formed on surface of the coating containing yttrium in comparison. Y enriched particle as corrosion product was observed on the top of alumina scale. The results indicated the beneficial influence of Y on the chemical stability of the protective scale in the presence of chloride. The mechanism was discussed.
منابع مشابه
AN INVESTIGATION ON EFFECT OF BOND COAT REPLACEMENT ON HOT CORROSION PROPERTIES OF THERMAL BARRIER COATINGS
In the present study NiCrAlY bond coating layer was produced by electroplating against common atmospheric plasma spraying (APS). Both types of the bond coats were applied on IN738LC base metal then, the YSZ (ZrO2-8% Y2O3) thermal barrier top layer was coated by atmospheric plasma spray technique. Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come ...
متن کاملHot Corrosion of Ti-Based Intermetallics with Coatings in NaCl+ (Na,K)2SO4 Melts at 750oC
In this study, the hot corrosion of TiAl, TiAlNb, and Ti3AlNb intermetallics with or without enamel coating and sputtered TiAlCr coating in (Na, K)2SO4 + NaCl melts at 750oC is investigated. The interfacial reaction between enamel and those alloys during hot corrosion has also been evaluated. The results indicate that severe corrosion of bare alloys occurs due to the self catalysis chlorination...
متن کاملHot corrosion behavior of HVOF-sprayed CoNiCrAlYSi coatings in a sulphate environment
HVOF-sprayed CoNiCrAlYSi coatings were tested at 900 °C in a hot corrosion environment containing sodium-potassium sulphates. The HVOF spraying caused the typical splat-on-splat structure. The results after the hot corrosion testing showed that the corrosion preferentially occurred at the coating surface and the splat boundaries. The oxidation along the splat boundaries can isolate the splat fr...
متن کاملHot Corrosion Behavior of Functional Graded Material Thermal Barrier Coating (RESEARCH NOTE)
In this paper a functional graded material (FGM) thermal barrier coating (TBC) is prepared using Atmospheric Plasma Spraying (APS) method. The FGM layers were deposited by varying the feeding ratio of CYSZ/NiCrAlY and conventional CYSZ on a NiCrALY-coated Inconel 738 substrates. Hot corrosion behavior, bonding strength and the related failure mechanisms of a conventional TBC and a FGM TBC are i...
متن کاملComputer Simulation Using Fuzzy Logic Model to Predict Hot Corrosion Kinetics in Molten Salt of Steel-T21 Coated by Simultaneous Yttrium-Doped Aluminizing-Siliconizing process
The present paper describes fuzzy logic simulation of an experimental study on the behavior of hot corrosion in molten salt (Na2SO4) of steel-T21 coated by simultaneous yttrium-doped aluminizing-siliconizingprocess . Diffusion coating was carried out at 1050C for 6 hr under Aratmosphere . The weight change measurements made on the coated steel during the cyclic tests are used to determine kinet...